Mohammad Reza JOZAGHKAR, Amir SEPEHRIAN AZAR, Farshid ZIAEE, Fakhrosadat MIRTALEB

Preparation, assessment, and swelling study of amphiphilic acrylic acid/chitosan-based semi-interpenetrating hydrogels

The aim of this study was to synthesize amphiphilic semi-IPN hydrogels based on acrylic acid (AA) and chitosan (CS) using AIBN as an initiator and N,N’methylene bis acrylamide as a crosslinking agent. The swelling behavior of the hydrogels was evaluated at a variety of pH values, temperature, the salinity of media and time, and the swelling mechanism was investigated using Fickian diffusion and Schott’s 2nd-order-kinetics models. FTIR spectroscopy was used to confirm the synthesis of AA/CS hydrogel. The swelling results showed that, in the acidic media, as the CS content increase the hydrogel swelling ratio reduces. It was found that the maximum swelling ratio (8550%) is attained for the sample HAC2 with an AA/CS ratio of 1:0.001 in the alkaline Ph value. It also revealed that the absorption capacity is directly dependent on the temperature and inversely related to the salt concentration. Besides, the absorption capacity of the synthesized hydrogels in the saline solution of $Na_2 SO_4$ was higher than NaCl.

PDF

___

1. Li SN, Li B, Yu ZR, Li Y, Guo KY et al. Constructing dual ionically cross-linked poly (acrylamide-co-acrylic acid)/chitosan hydrogel materials embedded with chitosan decorated halloysite nanotubes for exceptional mechanical performance. Composites Part B: Engineering 2020; 1 (194): 108046.
2. Li T, Hu X, Zhang Q, Zhao Y, Wang P et al. Poly (acrylic acid)-chitosan@ tannic acid double-network self-healing hydrogel based on ionic coordination. Polymers for Advanced Technologies 2020; 31 (7):1648-60.
3. Tian T, Bai Z, Wang B, Zhao S, Zhang Y. Facile fabrication of polyacrylic acid functionalized carboxymethyl chitosan microspheres for selective and efficient removal of Ni (II) from multicomponent wastewater. Colloids and Surfaces A: Physicochemical and Engineering Aspects 2020, 597: 124676.
4. Qi X, Tong X, Pan W, Zeng Q, You S et al. Recent advances in polysaccharide-based adsorbents for wastewater treatment. Journal of Cleaner Production 2021; 4: 128221.
5. Cui C, Shao C, Meng L, Yang J. High-strength, self-adhesive, and strain-sensitive chitosan/poly (acrylic acid) double-network nanocomposite hydrogels fabricated by salt-soaking strategy for flexible sensors. ACS applied materials & interfaces 2019; 11 (42): 39228-37.
6. Bhullar N, Rani S, Kumari K, Sud D. Amphiphilic chitosan/acrylic acid/thiourea based semi-interpenetrating hydrogel: Solvothermal synthesis and evaluation for controlled release of organophosphate pesticide, triazophos. Journal of Applied Polymer Science 2021; 138 (25): 50595.
7. Ge H, Wang S. Thermal preparation of chitosan–acrylic acid superabsorbent: Optimization, characteristic and water absorbency. Carbohydrate polymers 2014; 113: 296-303.
8. Shim JW, Nho YC. Preparation of poly (acrylic acid)–chitosan hydrogels by gamma irradiation and in vitro drug release. Journal of applied polymer science 2003; 90 (13): 3660-3667.
9. Zheng Y, Huang D, Wang A. Chitosan-g-poly (acrylic acid) hydrogel with crosslinked polymeric networks for Ni2+ recovery. Analytica chimica acta 2011; 687 (2): 193-200.
10. Jayaramudu T, Varaprasad K, Sadiku ER, Amalraj J. Temperature-sensitive semi-IPN composite hydrogels for antibacterial applications. Colloids and Surfaces A: Physicochemical and Engineering Aspects 2019; 572: 307-16.
11. Li S, Qin T, Chen T, Wang J, Zeng Q. Poly (vinyl alcohol)/poly (hydroxypropyl methacrylate-co-methacrylic acid) as pH-sensitive semi-IPN hydrogels for oral insulin delivery: preparation and characterization. Iranian Polymer Journal 2021; 30 (4): 343-53.
12. Takahashi A, Hamai K, Okada Y, Sakohara S. Thermosensitive properties of semi-IPN gel composed of amphiphilic gel and zwitterionic thermosensitive polymer in buffer solutions containing high concentration salt. Polymer 2011; 52 (17): 3791-3799.
13. Marjub MM, Rahman N, Dafader NC, Tuhen FS, Sultana S et al. Acrylic acid-chitosan blend hydrogel: a novel polymer adsorbent for adsorption of lead (II) and copper (II) ions from wastewater. Journal of Polymer Engineering. 2019, 39 (10): 883-91.
14. Paloma M, Torrado S, Torrado S. Interpolymer complexes of poly (acrylic acid) and chitosan: influence of the ionic hydrogel-forming medium. Biomaterials 2003, 24 (8):1459-68.
15. Achilleos M, Mpekris F, Stylianopoulos T, Krasia-Christoforou T. Structurally-defined semi-interpenetrating amphiphilic polymer networks with tunable and predictable mechanical response. RSC advances 2016; 6 (49): 43278-43283.
16. Liu S, Dong M, Zhang Z, Fu G. High elasticity, strength, and biocompatible amphiphilic hydrogel via click chemistry and ferric ion coordination. Polymers for Advanced Technologies 2017; 28 (9): 1065-70.
17. Ganguly S, Maity PP, Mondal S, Das P, Bhawal P et al. Polysaccharide and poly (methacrylic acid) based biodegradable elastomeric biocompatible semi-IPN hydrogel for controlled drug delivery. Materials Science and Engineering: C 2018; 92: 34-51.
18. Jozaghkar MR, Azar AS, Ziaee F. Preparation, Characterization, and swelling study of N, N’-dimethylacrylamide/acrylic acid amphiphilic hydrogels in different conditions. Polymer Bulletin, 2021; 3:1-3.
19. Zheng Y, Wang A. Evaluation of ammonium removal using a chitosan-g-poly (acrylic acid)/rectorite hydrogel composite. Journal of Hazardous Materials. 2009; 171 (1-3): 671-677.
20. Acik G, Karatavuk AO. Synthesis, properties and biodegradability of cross-linked amphiphilic Poly (vinyl acrylate)-Poly (tert-butyl acrylate) s by photo-initiated radical polymerization. European Polymer Journal 2020; 127: 109602.
21. Alwattar AA, Haddad A, Moore J, Alshareef M, Bartlam C et al. Heavy metal sensors and sequestrating agents based on polyaromatic copolymers and hydrogels. Polymer International 2021; 70 (1): 59-72.
22. Kanaan AF, Piedade AP, de Sousa HC, Dias AM. Semi-interpenetrating chitosan/ionic liquid polymer networks as electro-responsive biomaterials for potential wound dressings and iontophoretic applications. Materials Science and Engineering: C 2021; 121: 111798.
23. Chen T, Liu H, Dong C, An Y, Liu J et al. Synthesis and characterization of temperature/pH dual sensitive hemicellulose-based hydrogels from eucalyptus APMP waste liquor. Carbohydrate Polymers 2020; 247: 116717.
24. Gao M, Guo J, Cao H, Wang H, Xiong X et al. Immobilized bacteria with pH-response hydrogel for self-healing of concrete. Journal of environmental management 2020; 261: 110225.
25. Alonso GJ, Rivera JL, Mendoza AM, Mendez ML. Effect of temperature and pH on swelling behavior of hydroxyethyl cellullose-acrylamide hydrogel. e-Polymers. 2007; 7 (1): 1-10
26. Torrado S, Prada P, Paloma M, Torrado S. Chitosan-poly (acrylic) acid polyionic complex: in vivo study to demonstrate prolonged gastric retention. Biomaterials 2004; 25 (5): 917-23.
27. Ranjha NM, Ayub G, Naseem S, Ansari MT. Preparation and characterization of hybrid pH-sensitive hydrogels of chitosan-co-acrylic acid for controlled release of verapamil. Journal of materials science: Materials in Medicine 2010; 21 (10): 2805-16.
28. Jamali A, Moghbeli MR, Ameli F, Roayaie E, Karambeigi MS. Synthesis and characterization of pH‐sensitive poly (acrylamide-comethylenebisacrylamide-co-acrylic acid) hydrogel microspheres containing silica nanoparticles: Application in enhanced oil recovery processes. Journal of Applied Polymer Science 2020; 137 (12): 48491.
29. Kipcak AS, Ismail O, Doymaz I, Piskin S. Modeling and investigation of the swelling kinetics of acrylamide-sodium acrylate hydrogel. Journal of Chemistry, 2014.
30. Saraydın D, Öztop HN, Hepokur C. Nanocomposite smart hydrogel based on sepiolite nanochannels/N-isopropyl acrylamide/itaconic acid/ acrylamide for invertase immobilization. Polymer-Plastics Technology and Materials 2021; 60 (1): 25-36.
31. Guo X, Theissen S, Claussen J, Hildebrand V, Kamphus J et al. Dynamics of Sodium Ions and Water in Swollen Superabsorbent Hydrogels as Studied by $^{23}Na-and ^{1}H-NMR$. Macromolecular Chemistry and Physics 2019; 220 (2): 1800350.
32. Wang J, Fan X, Liu H, Tang K. Self-assembly and metal ions-assisted one step fabrication of recoverable gelatin hydrogel with high mechanical strength. Polymer-Plastics Technology and Materials 2020; 59 (17): 1899-909.