Lidia CRISTEA, Eufrosina OTLACAN, Enona CRISTEA

The study of the crystalline structure of the phases in the Al-Ni alloys ultrarapid solidification by the method of x ray diffraction

ISSN: 1300-5200
Yayın Aralığı: Yılda 4 Sayı
Başlangıç: 2018
Yayıncı: -

Melt -spinning and melt extraction methods of rapid solidification have been applied on Al-Ni alloys in the lower and higher composition. For orientate appreciations of the peripheric speed of the cooling disk it is used the dependence between the thickness of the solidified fibers and the peripheric speed of the extraction disk. The cooling speed calculated on the basis of the thermic transfer coefficient in accordance with the thickness of the fibers has lead to values of the cooling speed of the one million C/sec for fibres of 100 micrometers.Alloys with 1,86 % Ni content in pouring status and ultra-rapid solidificated have been analysed from the point of crystalline structure. The paper it's a short analysis of the use of the X-ray diffraction techniques for observing the effects of ultra-rapid solidification in Al-Ni alloys. This technique permit to observe highlighting the imperfections in the crystal pattern.

___

M. Hansen, K. Anderko, "Constitution of Binary Alloys", Mc Graw-Hill Book Comp., New York, 1958

H. L. Luo, C. C. Chao, P. Duwez, Trans. Met. Soc. AIME, 230 (1964), p. 1488

N. Petrescu s.a., Materials Science Forum, Zurich, vol. 225-227,1996, p. 317

Lidia Cristea, N. Petrescu, Enona Cristea, Experimental researches on the extension of Ni solubility in Al by melt quenching, EUROMAT 2001, Rimini, Italy, 2001, p.307

Lidia Cristea, Enona Cristea, Thre ultrarapid solidification applied to the system Al-Ni, EUROMAT 2003, Lausanne, Switzerland