Octahedral-like NiFe2O4 ferrite nanocrystals were synthesized using EDTA-assisted hydrothermal method under mild conditions. XRD and FTIR analysis were used for composition and structure investigation. XRD analysis revealed a pure ferrite phase with high crystallinity. Morphological investigation by SEM showed octahedral nanocrystals with an average particle size of \sim 40 nm. Crystallite size calculated from XRD peak broadening resulted in an average crystallite size of 39 nm, matching well with the SEM observations. TEM analysis and corresponding electron diffraction confirmed the octahedral morphology and single crystallinity of octahedral nanoparticles. Magnetic measurements showed that NiFe2O4 octahedrons have smaller coercivity than bulk ferrite due to the low shape anisotropy.

Octahedral-like NiFe2O4 ferrite nanocrystals were synthesized using EDTA-assisted hydrothermal method under mild conditions. XRD and FTIR analysis were used for composition and structure investigation. XRD analysis revealed a pure ferrite phase with high crystallinity. Morphological investigation by SEM showed octahedral nanocrystals with an average particle size of \sim 40 nm. Crystallite size calculated from XRD peak broadening resulted in an average crystallite size of 39 nm, matching well with the SEM observations. TEM analysis and corresponding electron diffraction confirmed the octahedral morphology and single crystallinity of octahedral nanoparticles. Magnetic measurements showed that NiFe2O4 octahedrons have smaller coercivity than bulk ferrite due to the low shape anisotropy.