Bir fretting yorulma cihazının tasarımı ve imalatı

Fretting, küçük genlikli salınımlı bağıl harekete sahip ve mekanik olarak temasta bulunan iki yüzey arasında meydana gelen bir aşınma sürecidir. Bu çalışmada, fretting mekanizması ve buna tesir eden faktörler ile ilgili olarak yapılan araştırmalar incelenmiş ve bu çalışmalar doğrultusunda, fretting yorulma deneylerinin yapılabileceği bir deney düzeneği tasarlanıp imal edilmiştir. Ayrica bu deney düzeneğinde yapılan örnek bir çalışma verilmiştir.

The manufacturing and design of a fretting fatigue apparatus

Fretting is a wear process of two mechanically contacted surfaces which are subject to a relative micro amplitute motion. In this study, the surveys related in fretting were compiled and the fretting fatigue machine was designed and manufactured. In addition a sample study was given as an example done at this machine

___

  • 1. Zhang, X., Zhang, C., ve Zhu, C., Slip Amplitude Effects and Microstructural Characteristics of Surface Layers In Fretting Wear of Carbon Steel, Wear, 134, 297-309.1989
  • 2. Bryggman, U., ve Soderberg, S., Contact Condition in Fretting. Wear, 107, 245, 19863. Brady, B. G., Fretting Wear. SAE. Technical Paper Series. Aerospace Technology Conference and Exposition Long Beach.Aralık 1-4. California, 1990
  • 4. Troshchenko, V. T., Tsybanev, G.V., ve Khotsyanovskıı, A. O., Life of Steels in Fretting Fatigue. Plenum Publishing Corporation. Academy Of Sciences Of The Ukrainian, Kiev, 1989
  • 5. Waterhause, R. B., Theories of Fretting. Fretting Fatigue. Applied Science Pub. Ltd. Ripple Road, Barking, Essex, 1981
  • 6. Hurricks, P. I., The Mechanism of Fretting - A Review. Wear. 15, 389, 1970
  • 7. Suh, N. P., The Delamination Theory of Wear, Wear. 25, 111, 1973
  • 8. Waterhause, R. B., ve Taylor, D. E., Fretting Debris And The Delamination Theory of Wear. Wear. 29, 337, 1974
  • 9. Sproles, E. S., Duquette, D. J., The Mechanism of Material Removal in Fretting. Wear. 49, 339, 1978
  • 10. Soderberg, S., Colvın, T., Salama, K., ve Vıngsbo, 0., Ultrasonic Fretting Wear of A Plain Carbon Steel. Journal Of Engineering Materials And Technology. 108,153,1986
  • 11. Sodeberg, S., Bryggman, U., Ve Mc Cullough, I., Frequency Effects in Fretting Wear. Wear. 110,19,1986
  • 12. Waterhause, R. B., Fretting Wear. Wear. 100,107, 1984
  • 13. Ohmae, N., ve Isukızoe, I., The Effect Of Slip Amplitude On Fretting. Wear. 27, 281, 1974
  • 14. Kayaba, T., ve Iwabuchi, A., The Influence of Hardness on Fretting Wear. JSLE. 24, 598, 1979
  • 15. Sato, J., Shıma, M., ve Sugawara, T., A Fundamental Study of Fretting Damage to Glass Using An Improved Apparatus.Wear. 106,53, 1985
  • 16. Kennedy, P. J., Peterson, M. B., ve Stallıngs, L., An Evaluation Of Fretting at Small Slip Amplitudes. ASTM. Stp - 780, 3, 1982
  • 17. Kennedy, P. J., Stallings, L., Peterson, M. B., A Study of Surface Damage at Low Amplitude Slip. Asle. Trans. 27,305, 1984
  • 18. Gaul, D. J., ve Duquette, D. J., The Effect of Fretting and Environment on Fatigue Crack Initation and Early Propagation in A Quenched and Tempered 4130 Steel. Metallurgical Trans, 11a, 1555, 1980
  • 19. Reeves, R.K., ve Hoepner, D.W., Microstructural and Environmental Effects on Fretting Fatigue. Wear. 47, 221, 1978
  • 20. Reeves, R. K., ve Hoeppner, D. W., Scanning Electron Microscope Analysis Of Fretting Fatigue Damage. Wear. 48, 87, 1987
  • 21. Waterhause, R.B., Fretting Corrosion. Pergamon Press. Oxford, 1972
  • 22. Waterhause, R. B., ve Taylor, D. E, The Initation of Fatigue Cracks in A % 0,7 Carbon Steel By Fretting. Wear. 17, 139, 1971
  • 23. Bill, R. C., Review of Factors That Influence Fretting Wear. ASTM. Stp-780, 165, 1982
  • 24. Stott. F. H., Lın, D. S., ve Wood, G. C, The Structure and Mechanism of Formation of The Glaze Oxide Layers Produced on Nickel Based Alloys During Wear At High Temperature. Corrosion Science. 13, 449,1973
  • 25. Endo, K., ve Goto, H., Initation and Propagation of Fretting Fatigue Cracks. Wear. 38,311,1976
  • 26. Sato, J., Shima, M., Igarashı, J., Tanaka, M., ve Waterhause, R. B., Studies on Fretting. 1. Section, JSLE. 26, 207.1981
  • 27. Hoeppner, D. W., Environmental Effects in Fretting Fatigue. Fretting Fatigue. Applied Science Publishers Ltd. London, 1981
  • 28. Kovalevskıı, V. V., The Mechanism of Fretting Fatigue in Metals. Wear. 67, 271, 1981
  • 29. Alıc, J. A., Hawley, A. L., ve Urey, J. M., Formation of Fretting Fatigue Cracks in 7075 Aluminium Alloy. Wear. 56. 351, 1979
  • 30. Dobromırskı, J., ve Smith I.O., Metallographic Aspects Of Surface Damage, Surface Temperature and Crack Initation in Fretting Fatigue. Wear. 117, 347, 1987
  • 31. Sato, K., Fuji, H., ve Kodama, S., Crack Propagation Behaviour in fretting Fatigue. Wear. 107,245, 1986
  • 32. Stowers, I. F., ve Rabinowicz, E., The Mechanism of Fretting Wear. Trans. Asme. J. Lubrication Technology. 65, 1973
  • 33. Nowell, D., Hills, D. A., ve O'connor, J. J., An Analysis of Fretting Fatigue. Proc. Int. Conf. On Tribology. Inst. Mechanical Engineers. 965, 1987
  • 34. Fu, Y., Wei, J., Batchelor, W., Some Considerations on the Mitigation of Fretting Damage By The Application Surface- Modification Technologies, Journal of Materials Processing Technology 99, 231-245, 2000