Synthesis of Ceramic Particles (Al2O3 and TiB2) in Aluminum Matrix

Al2O3 ve TiB2 partiküller, sıcak presleme yöntemi sayesinde in situ reaksiyonlarla alüminyum matris içindebaşarıyla sentezlenmişlerdir. İşlem parametreleri; sinterleme sıcaklığı 900-1000oC, soğuk presleme basıncı: 7 MPasıcak presleme basıncı: 1 MPa ve fırında bekletme süresi 5-10 dakika olarak seçilmiştir. Kompozit mikroyapıları vetakviye partikül sayı-boyutları SEM ve EDS analizleri vasıtasıyla belirlenmiştir. Analiz sonuçlarına göre; literatürdesıkça rastlanan gevrek Al3Ti intermetalik geçiş fazı elimine edilebilmiştir.

Anahtar Kelimeler:

In situ, kompozit, sinterleme, takviye elemanı

Synthesis of Ceramic Particles (Al2O3 and TiB2) in Aluminum Matrix

Al2O3 and TiB2 particles have been successfully synthesized in aluminum matrix with in situ reactionsby hot pressing method. Process parameters; sintering temperatures 900-1000oC, pressure of cold pressing: 7 MPahot pressing: 1 MPa and holding times in furnace 5-10 minutes were selected. Composite microstructures andreinforcement particle numbers-sizes were investigated via SEM and EDS analysis. According to the analysisresults; brittle Al3Ti intermetallic transition phase frequently encountered in the literature could be eliminated.

Keywords:

Composite, in situ, reinforcement particle, sintering,

PDF

___

Balci O, Agaogullari D, Gokce H, Duman I, Ovecoglu LM, 2014. Inﬂuence of TiB 2 particle size on the microstructure and properties of Al matrix composites prepared via mechanical alloying and pressureless sintering. Journal of Alloys and Compounds, 586: 78-84.
Chen W, Xiao H, Fu Z, Fang S, Zhu D, 2013. Reactive hot pressing and mechanical properties of TiAl3/Ti3AlC2/Al2O3 in situ composite. Materials and Design, 49: 929–934.
Chu MG, Premkumar MK, 1993. Mechanism of TiC formation in Al/TiC in situ metal-matrix composites. Metallurgical and Materials Transactions A, 24 (12): 2803-2805.
Dikici B, Gavgali M, Bedir F, 2010. Synthesis of in situ TiC particles in liquid aluminum: the effect of sintering temperature. Journal of Composite Materials, 45 (8): 895-900.
Dikici B, Gavgali M, 2013. The effect of sintering time on synthesis of in situ submicron α-Al 2O3 particles by the exothermic reactions of CuO particles in molten pure Al. Journal of Alloys and Compounds, 551: 101-107.
Elrakayby H, Kim HK, Hong SS, Kim KT, 2015. Investigation of densifcation behavior of nickel alloy powder during hot isostatic pressing. Advanced Powder Technology, 26: 1314–1318.
Jun D, Liu YH, Yu SR, Li WF, 2004. Dry sliding friction and wear properties of Al2O3 and carbon short fbres reinforced Al- 12Si alloy hybrid composites. Wear, 257: 930-940.
Onal M, Gavgali M, 2015. In situ aluminum metal matrix composites and their production by hot pressing. Journal of Science and Technology, Ordu University, 5 (2): 63-73.
Sharif ME, Karimzadeh F, Enayati HM, 2011. Preparation of Al2O3- TiB 2 nanocomposite powder by mechanochemical reaction between Al, B2O3 and Ti. Advanced Powder Technology, 22: 526-531.
Zhu H, Wang H, Ge L, Chen S, Wu S, 2007. Formation of composites fabricated by exothermic dispersion reaction in Al-TiO 2-B2O3 system. Trans. Nonferrous Met. Soc. China, 17: 590-594.
Zhu H, Wang H, Ge L, Xu W, Yuan Y, 2008. Study of microstructure and mechanical properties of composites fabricated by the reaction method in an Al-TiO 2-B2O3 system. Materials Science and Engineering A, 478: 87–92.
Kayikci R, Savas O, Kurtulus O, 2009. AlB2/Al composite production boron oxid with added research. 5. International Advanced Technology Symposium (IATS’09), 13-15 May 2009, Karabuk, Turkey.
Kok M, 2006. Abrasive wear of Al2O3 particle reinforced 2024 aluminum alloy composites fabricated by vortex method. Composites: Part A, 37: 457–464.
Kurt A, 1992. Properties of powder metal bronze bearings. Gazi University, Institute of Natural and Applied Sciences, (Printed) Master Thesis, 124 p.
Lu L, Lai OM, Su Y, Teo LH, Feng FC, 2001. In situ TiB2 reinforced Al alloy composites. Scripta Materialia, 45: 1017-1023.
German MR, 2013. Sintering Theory and Practice Book. First Edition, Pennsylvania, USA. 550 p.