Plasma-initiated polimerization of (2-methacryloyloxyethyl) thrimethyl ammonium chloride
Plasma-initiated polimerization of (2-methacryloyloxyethyl) thrimethyl ammonium chloride
Plasma-initiated polymerization of (2-methacryloyloxyethyl) thrimethyl ammonium chloride (MTAC))was studied. The effects of discharge time and discharge power on temperature in a tubular-type reactor chamber were accurately tested by on-line thermocouple, and the equation relating discharge time, discharge power and temperature in the tubular-type reactor chamber was derived. The results indicated that temperature played a very important role in controlling the solubility of Poly(MTAC) in water. For T $geq$ 130°, Poly (MTAC) was cross-linked, and the highest rate of absorbing water of Poly(MTAC) was 15 g-g"1. For T < 130°, Poly(MTAC) was linear, and the highest intrinsic viscosity of Poly(MTAC) was 420.2 $cm^3.g^{-1}$. The polymerization condition of linear Poly(MTAC) was optimized as follows: discharge time 60 s and discharge power 60 W.
___
- 1. J. Chen, "Plasma Chemistry and Application". Science Press of China, 2001.
- 2. X. Ge, Q. Ye and X. Xu, Radiat. Phys. Chem. 50, 253, (1997).
- 3. T. Okada, I. Ishigaki, T. Suma, and S. Machi, J. Appl. Polym. Sci. 24, 1713 (1979)
- 4. H. Susanna, A. Toni, K. Lauri, Polymer, 44, 7909 (2003).
- 5. L. Zhang, X. Liu and C. Li, Polymer Mater. Science and Engineering, 15, 59 (1999).
- 6. W. Zhang and X. Hou, Acta Polymerica Sinica, 10, 577 (2000).
- 7. Z. Cheng and J. Lu, L. Fine Chemicals, 17, 658 (2000).
- 8. C. Chelaru, I. Diaconu and I. Simionescu, Polymer Bulletin, 40, 757 (1998).