New Aromatic Polyamide with Azo and Phosphine Oxide Groups in the Main Chain
A new flame-retardant polyamide containing phosphine oxide and azobenzene moieties in the main chain was synthesized by the solution polycondensation reaction of 4,4`-azodibenzoic acid with bis(3-aminophenyl) phenyl phosphine oxide using thionyl chloride, N-methyl-2-pyrrolidone and pyridine. This new polymer was obtained in high yield (96%) and showed high inherent viscosity (0.55 dL/g) and was characterized by elemental analysis, FT-IR spectroscopy, thermal gravimetric analysis (TGA and DTG) and solubility test. Furthermore, another polyamide was prepared by solution polycondensation reaction of 4,4`-azodibenzoic acid with 1,4-phenylene diamine and its flame-retardant behavior was compared by the use of the LOI with the previous one.
New Aromatic Polyamide with Azo and Phosphine Oxide Groups in the Main Chain
A new flame-retardant polyamide containing phosphine oxide and azobenzene moieties in the main chain was synthesized by the solution polycondensation reaction of 4,4`-azodibenzoic acid with bis(3-aminophenyl) phenyl phosphine oxide using thionyl chloride, N-methyl-2-pyrrolidone and pyridine. This new polymer was obtained in high yield (96%) and showed high inherent viscosity (0.55 dL/g) and was characterized by elemental analysis, FT-IR spectroscopy, thermal gravimetric analysis (TGA and DTG) and solubility test. Furthermore, another polyamide was prepared by solution polycondensation reaction of 4,4`-azodibenzoic acid with 1,4-phenylene diamine and its flame-retardant behavior was compared by the use of the LOI with the previous one.