Effect of CMC and HPC mixture on the photocatalytic activity of Nd-$TiO_2/SiO_2$ film under visible light irradiation
Effect of CMC and HPC mixture on the photocatalytic activity of Nd-$TiO_2/SiO_2$ film under visible light irradiation
Neodymium-titania/silica films were prepared by the sol-gel method with the addition of various amounts of hydroxy propyl cellulose (HPC) and 5.09 × $10^{-5}$ g $g^{-1}$ solution of carboxy methyl cellulose (CMC) in saturated conditions. The porous Nd-$TiO_2/SiO_2$was obtained after heat treatment for 2 h at 500 ◦ C, with the surface area up to 276 m2 $g^{-1}$ , which was measured using the Brunauer, Emmett, and Teller (BET) method. Scanning electron microscopy (SEM) showed that the particle size of Nd-$TiO_2/SiO_2$ decreased and the microstructure of the film became loose in suitable conditions with the addition of CMC to HPC. Subsequently, the photocatalytic activity of Nd-$TiO_2/SiO_2$ film under visible light irradiation was achieved to an optimum when the concentrations became 3.825 × $10^{-3}$ and 5.09 × $10^{−5}g $g^{-1}$ sol. for HPC and CMC, respectively.
___
- 1. Agarwala, S.; Ho, G. W. Mater. Lett. 2009, 63, 1624-1627.
- 2. Li, H.; Wang, J.; Li, H.; Yin, S.; Sato, T. Mater. Lett. 2009, 63, 1583-1585.
- 3. Ohno, T.; Numakura, K.; Itoh, H.; Suzuki, H.; Matsuda, T. Mater. Lett. 2009, 63, 1737-1739.
- 4. Hafez, H. S. Mater. Lett. 2009, 63, 1471-1474.
- 5. Wetchakun, N.; Phanichphant, S. Curr. Appl. Phys. 2008, 8, 343-346.
- 6. Euvananont, C.; Junin, C.; Inpor, K.; Limthongkul, P.; Thanachayanont, C. Ceram. Int. 2008, 34, 1067-1071.
- 7. Nizard, H.; Kosinova, M. L.; Fainer, N. I.; Rumyantsev, Yu. M.; Ayupov, B. M.; Shubin, Yu. V. Surf. Coat. Tech. 2008, 202, 4076-4085.
- 8. Zhao, G.; Tian, Q.; Liu, Q.; Han, G. Surf. Coat. Tech. 2005, 198, 55-58.
- 9. Ghigna, P.; Speghini, A.; Bettinelli, M. J. Solid State Chem. 2007, 180, 3296-3301.
- 10. Arroyo, R.; Cordoba, G.; Padilla, J.; Lava, V. H. Mater. Lett. 2002, 54, 397-402.
- 11. Anpo, M.; Takeuchi, M. J. Catal. 2003, 216, 505-516.
- 12. Depero, L.; Sagaletti, L.; Allieri, B.; Bontempi, M.; Marino, L. E.; Zachii, M. J. Cryst. Growth 1999, 198, 516-520.
- 13. Kubacka, A.; Col´on, G.; Fern´andez-Garc´ıa, M. Catal. Today 2009, 143, 286-292.
- 14. Kubacka, A.; Fernandez-Garcıa, M.; Col´on, G. J. Catal. 2008, 254, 272-284.
- 15. Zhu, J.; Chen, F.; Zhang, J.; Chen, H.; Anpo, M. J. Photochem. Photobiol. 2006, 180, 196-204.
- 16. Adan, C.; Bahamonde-Santos, A.; Fernandez-Garcıa, M.; Martınez-Arias, A. Appl. Catal. B 2007, 72, 11-17.
- 17. Carnerio, J. O.; Teixeira, V.; Portinha, A.; Magalhaes, A.; Coutinho, P.; Tavares, C. J. et al. Mater. Sci. Eng. B 2007, 138, 144-150.
- 18. Colon, G.; Hidalgo, M. C.; Navıo, J. A. Appl. Catal. A Gen. 2002, 231, 185-199.
- 19. Colon, G.; Maicu, M.; Hidalgo, M. C.; Navio, J. A. Appl. Catal. B Environ. 2006, 67, 41-51.
- 20. Rengaraj, S.; Venkataraj, S.; Yeon, J. W.; Kim, Y.; Li, X. Z.; Pang, G. K. H. Appl. Catal. B Environ. 2007, 77, 157-165.
- 21. Parida, K. M.; Sahu, N. J. Mol. Catal. A Cheml. 2008, 287, 151-158.
- 22. Burns, A.; Hayes, G.; Li, W.; Hirvonen, J.; Derek Demaree, J.; Ismat Shah, S. Mater. Sci. Eng. B 2004, 111, 150-155.
- 23. Guan, K.; Lu, B.; Yin, Y. Surf. Coat. Tech. 2003, 173, 219-223.
- 24. Guan, K. Surf. Coat. Tech. 2005, 191, 155-160.
- 25. Houmard, M.; Riassetto, D.; Roussel, F.; Bourgeors, A.; Berthome, G.; Joud, J. C. et al. Appl. Surf. Sci. 2007, 254, 1405-1414.
- 26. Enomoto, N.; Kawasaki, K.; Yoshida, M.; Li, X.; Uehara, M.; Hojo, J. Solid State Ionics 2002, 151, 171-175.
- 27. Liu, Z.; Zhang, X.; Murakami, T.; Fujishima, A. Sol. Energy Mater. Sol. Cells 2008, 92, 1434-1438.
- 28. Ye, X.; Zhou, Y.; Chen, J.; Sun, Y. Mater. Chem. and Phys. 2007, 106, 447-451.
- 29. Gao, W.; Chen, J.; Guan, X.; Jin, R.; Zhang, F.; Guan, N. Catal. Today 2004, 93-95, 333-339.
- 30. Zheng, M.; Gu, M.; Jin, Y.; Jin, G. Mater. Sci. Eng. B 2000, 77, 55-59.
- 31. Jiao, J.; Xu, Q.; Li, L. J. Colloid Inter. Sci. 2007, 316, 596-603.