Impact of Impregnation with Imersol-Aqua on the Yellow Color Tone of Some Woods and Varnishes
This study was performed to determine the effects of impregnation on the yellow color tone (YCT) of some woods and varnishes. For this purpose, the test specimens prepared from Oriental beech (Fagus orientalis Lipsky) and oak (Quercus petrea Liebl.) according to ASTM D 358 were impregnated with Imersol-Aqua according to ASTM D 1413-99 and the manufacturer's instructions by short-term, medium-term, and long-term dipping, and were then coated with synthetic, acrylic, waterborne, and polyurethane varnishes according to ASTM D 3023. The YCT of test specimens after the varnishing process was determined according to ASTM D 2244-02. As a result, the highest YCT value was obtained in oak, with medium-term dipping and synthetic varnish, whereas the lowest YCT was in Oriental beech with long-term dipping and waterborne varnish. Considering the interaction of wood type, period of impregnation, and type of varnish, YCT was the highest in oak + short-term dipping + synthetic varnish, and the lowest in Oriental beech + short-term dipping + waterborne varnish. Varnishing increased the YCT in oak and Oriental beech, but impregnation period increased the color tone in Oriental beech and decreased it in oak. This effect must be taken into consideration in applications where the YCT of wood is important.
Impact of Impregnation with Imersol-Aqua on the Yellow Color Tone of Some Woods and Varnishes
This study was performed to determine the effects of impregnation on the yellow color tone (YCT) of some woods and varnishes. For this purpose, the test specimens prepared from Oriental beech (Fagus orientalis Lipsky) and oak (Quercus petrea Liebl.) according to ASTM D 358 were impregnated with Imersol-Aqua according to ASTM D 1413-99 and the manufacturer's instructions by short-term, medium-term, and long-term dipping, and were then coated with synthetic, acrylic, waterborne, and polyurethane varnishes according to ASTM D 3023. The YCT of test specimens after the varnishing process was determined according to ASTM D 2244-02. As a result, the highest YCT value was obtained in oak, with medium-term dipping and synthetic varnish, whereas the lowest YCT was in Oriental beech with long-term dipping and waterborne varnish. Considering the interaction of wood type, period of impregnation, and type of varnish, YCT was the highest in oak + short-term dipping + synthetic varnish, and the lowest in Oriental beech + short-term dipping + waterborne varnish. Varnishing increased the YCT in oak and Oriental beech, but impregnation period increased the color tone in Oriental beech and decreased it in oak. This effect must be taken into consideration in applications where the YCT of wood is important.
___
- Anderson, E.L., Z. Pawlak, N.L. Owen and W.C. Feist. 1991. Infra yellow studies of wood weathering. Appl. Spectroscopy. 45: 641- 647.
- ASTM D 358, 1983. Wood to be used as panels in weathering test of coating. ASTM Standards. West Conshohocken. PA. USA.
- ASTM D 1413-99, 1999. Standard test method for wood preservatives by laboratory soil-block cultures. ASTM Standards. West Conshohocken. PA. USA.
- ASTM D 2244-02, 2003. Standard practice for calculation of color tolerances and color differences from instrumentally measured color coordinates. ASTM Standards. West Conshohocken. PA. USA.
- ASTM D 3023, 1981. Practical for determination of resistance of factory applied coating on wood product of stain and reagents. ASTM Standards. West Conshohocken. PA. USA.
- Atar, M. 1999. Renk Açıcı Kimyasal Maddelerin Ağaç Malzemede Üst Yüzey İşlemlerine Etkileri. Doktora Tezi. Gazi Üniversitesi, Fen Bilimleri Enstitüsü. p.120-121.
- Cassens, D.L. and W.C. Feist. 1999. Exterior wood in the south: selection, application and finishes. USDA Forest Service. Fpl-Gtr- 69: 55.
- Çakıcıer, N. and A. Sönmez. 1996. Ahşap yüzeylerde kullanılan verniklerin su ile eritilen önemli ağaç boyaları ile boyanmış yüzeylerde yaptığı renk değişiklikleri. Endüstriyel Teknoloji. 2: 34-40.
- DYO, 1996. Dewilux Teknik Bülten. Dewilux Fabrikaları. A.Ş. İzmir.
- Evans, P.D., A.J. Michell and K. Schmalzl. 1992. Studies of the degradation and protection of wood surfaces. Wood Sci. Technol. 26: 151-163.
- Hickson’s Timber Impregnation Co. Ltd., 2000. Into the 21stcentury Imersol-Aqua brochure. Datasheet no: 6214, 2.0.0, P.1-4, USA.
- Örs, Y., M. Atar and A. Özçiftci. 2000. Bonding strength of polyvinyl acetate based adhesive in some wood materials treated with impregnation. Journal of Applied Polymer Science. 76: 1472- 1479.
- Shigo, A.L. and W.E. Hills. 1973. Heartwood, discolor yellow wood and microorganism in living trees. Annual Review Phytopathol. 11: 197-222.
- TS 2472, 1976. Odunda fiziksel ve mekanik deneyler için hacim ağırlığı tayini. Türk Standartları Enstitüsü. Ankara.
- TS 2471, 1976. Odunda fiziksel ve mekanik deneyler için rutubet miktarı tayini. Türk Standartları Enstitüsü. Ankara.
- TS 344, 1981. Ahşap koruma genel kuralları. Türk Standartları Enstitüsü. Ankara.
- TS 345,1974. Ahşap emprenye maddeleri etkilerinin muayene metotları. Türk Standartları Enstitüsü. Ankara.
- Uysal, B., A. Sönmez, M. Atar and A. Özçifçi. 1999. Ağaç malzemede renk açma işlemleri ve verniklerin renk değiştirici etkileri. Turk J. Agric. For. 23: 849-854.
- Uysal, B., H. Peker and M. Atar. 1998. Açık hava Şartlarının emprenyelenmiş ve verniklenmiş ağaç malzeme yüzeyinde renk değişimine etkileri. Teknoloji Dergisi. 1: 66-77.