Gökay NEMLİ, Gürsel ÇOLAKOĞLU

Effects of Mimosa Bark Usage on Some Properties of Particleboard

The objective of this study was to determine the effect of mimosa bark usage on the formaldehyde emission, physical and mechanical properties of particleboard. Fifteen panels from black locust (Robinia pseudoacacia L.) wood containing mimosa bark in a core layer at different ratios were manufactured. Three boards without bark addition were produced as control boards. Formaldehyde emission, modulus of rupture, modulus of elasticity, internal bond strength and thickness swelling of the specimens were tested. It was found that panels made from black locust wood had the highest mechanical properties while panels containing mimosa bark had the lowest. Bark usage significantly improved (decreased) the formaldehyde emission and thickness swelling of particleboard. Based on the findings of this study, it appears that mimosa bark can be used in the manufacture of particleboard panels. Bark content was found to be a raw material parameter influencing the properties of the panels.

Anahtar Kelimeler:

Particleboard, mimosa bark, formaldehyde emission, mechanical properties, physical properties.

Effects of Mimosa Bark Usage on Some Properties of Particleboard

Keywords:

Particleboard, mimosa bark, formaldehyde emission, mechanical properties, physical properties.,

PDF

___

Blanchet, P., A. Cloutier and B. Riedl. 2000. Particleboard made from hammer milled black spruce bark residues. Wood Science and Technology, 34: 11-19.
Chen, T.Y. and M. Paulitsch. 1974. Inhalstoffe von nadeln, ride und holz der fichte und kiefer und ihr einfluss auf die eigenschaften daraus hergesteller spanplatten. Holz als Roh und Werkstoff, 32: 394- 401.
DIN EN 717-3. 1996. Holzwerkstoffe bestimmung der formaldehydabgabe Teil 3: formaldehydabgabe nach der Flaschen methode.
EN 310. 1993. Wood based panels, determination of modulus of elasticity in bending and bending strength. European Standardization Committee, Brussels.
EN 317. 1993. Particleboards and fiberboards, determination of swelling in thickness after immersion. European Standardization Committee, Brussels.
EN 319. 1993. Particleboards and fiberboards, determination of tensile strength perpendicular to plane of the board. European Standardization Committee, Brussels.
EN 312-2. 1996. Particleboards-Specifications-Part 2: Requirements for general-purpose boards for use in dry conditions. European Standardization Committee, Brussels.
EN 312-3. 1996. Particleboards-Specifications-Part 3: Requirements for boards for interior fitments (including furniture) for use in dry conditions. European Standardization Committee, Brussels.
Hall, H.J., R.O. Gertjajensen, E.L. Schimidt, C.G. Carled and R.C. DeGroot. 1984. Preservative effect on mechanical and thickness swelling properties of aspen wafer board. Proceedings of a Workshop on Durability of Structural Panels, Pensocola, USA.
Kalaycıoğlu, H. and G. Nemli. 1997. Properties of structural particleboard prepared from the bark of pinus brutia. Proceedings of XI. World Forestry Congress, pp. 50, Antalya, Turkey.
Lehmann, W.F. and R.L. Geimer. 1974. Properties of structural particleboards from douglas-fir forest resudies. Forest Products Journal, 24: 17-25.
Lelis, R. and E. Roffael. 1995. Über die reaktivitat von douglasiensplint- und-kernhoz und deren heisswasserextrake gegenüber formaldehyd. Holz als Roh und Werkstoff, 53: 12-16.
Nemli, G. 1995. Effects of melamine impregnated paper coating on the technological properties of particleboard. MSc. Thesis, Faculty of Foresty, Karadeniz Technical University, 89 pp., Trabzon, Turkey (in Turkish).
Nemli, G. 2000. Effects of surface coating materials and process parameters on the technological of particleboard. PhD Thesis, Faculty of Foresty, Karadeniz Technical University, 181 pp., Trabzon, Turkey (in Turkish).
Nemli, G., H. Kırcı and A. Temiz. 2004. Influence of impregnating wood particles with mimosa bark extract on some properties of particleboard. Industrial Crops and Products, 20: 339-344.
Prasetya, B. and E. Roffael. 1991. Untersuchenegen über das verhalten extraktstoffreicher rinden in holzspanplatten zur reaktivitat de fichtenrinde gegenüber formaldehyd. Holz als Roh und Werkstoff, 49: 341-344.
Reineke, L.H. 1965. Use for forest resudies. Res. Note FPL-092. USDA Serv., Forest Products Laboratory, Madison. WI, USA.
Roffael, E. 1982. Die formaldehydabgabe von spanplatten und anderen werkstoffen. DRW-Werlag, Stuttgart.
Tisler, V., E. Galla and E. Pulkkinen. 1986. Fractionation of water extract from picea abies bark. Holz als Roh und Werkstoff, 44: 427-431.
Volz, K.R. 1973. Herstellung und eigenschafteen von fichen-kiefer-und buchrindenplatten. Holz als Roh und Werkstoff, 31: 221-229.
Vyse, B. 1993. European formaldehyde regulations. European Plastic Laminates Forum, pp. 107-111. Köln-Germany.
Wisherd, K.D. and B. Wilson. 1979. Bark as a supplement to wood furnish for particleboard. Forest Products Journal, 29: 35-40.