A COMPARATIVE STUDY ON THE PHYSICAL AND MECHANICAL PROPERTIES OF ALKALI ACTIVATED MATERIALS

In this study, the effect of silica modulus (MS) on the properties of alkali activated material (AAM) was evaluated. The precursor material selected for the production of AAM was a blend of ground granulated blast furnace slag (GGBFS) and fly ash (FA). The activator was a mix of sodium hydroxide and sodium silicate having different silica modulus and constant Na2O dosage of 4% by mass of GGBFS and FA. The experimental study investigated the basic mechanical and physical properties of the mortars such as compressive strength, flexural strength, void ratio, water absorption, and density. Test results showed that the physical properties of the AAM mixes such as water absorption and voids content were higher compared to the OPC mix, however, the oven-dry density values were at similar levels, indicating that within the scope of this study at similar density, the AAM produces a more porous microstructure. The compressive strength of the AAM mix having silica modulus of 1.0 (AAM-1.0) was comparable to the OPC mortar at 3 and 7 days however at 28 days the OPC mix possessed significantly higher strength. The AAM mixes produced a lower flexural strength compared to the OPC mix at 28 days and the flexural to compressive strength ratio was almost halved in the AAM mixtures.

Keywords:

Alkali activated material, ground granulated blast furnace slag, fly ash, silica modulus physical properties, mechanical properties,

PDF

___

[1] Provis J.L., van Deventer J., (2014) Alkali-Activated Materials, State of Art Report. RILEM TC 224-AAM.
[2] Neville A.M., (2011) Properties of concrete. Pearson Education Limited, Essex, England.
[3] Pacheco-Torgal F., Labrincha J.A., Leonelli C., Palomo A., Chindaprasirt P., (2015) Handbook of Alkali-Activated Cements, Mortars and Concretes. Elsevier, Woodhead Publishing.
[4] Turner L.K., Collins F.G., (2013) Carbon dioxide equivalent (CO2-e) emissions: A comparison between geopolymer and OPC cement concrete, Construction and Building Materials 43, 125-130.
[5] ASTM C 125, (2019) Standard Terminology Relating to Concrete and Concrete Aggregates, ASTM International, West Conshohocken, United States.
[6] ASTM C 618-05, (2019) Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete, ASTM International, West Conshohocken, United States.
[7] Puertas F., Gonzalez-Fonteboa B., Gonzalez-Taboada I., Alonso M.M., Torres-Carrasco M., Rojo G., Martínez-Abella F., (2018) Alkali-activated slag concrete: Fresh and hardened behavior, Cement and Concrete Composites 85, 22-31.
[8] Aktürk B., Kizilkanat A.B., Kabay N., (2019) Effect of calcium hydroxide on fresh state behavior of sodium carbonate activated blast furnace slag pastes, Construction and Building Materials 212, 388-399.
[9] Aktürk B. , Nayak S., Das S., Kızılkanat A. B., (2019) Microstructure and Strength Development of Sodium Carbonate Activated Blast Furnace Slags, Journal of Materials in Civil Engineering 31, 1-11.
[10] Bakharev T., Sanjayan J.G., Cheng Y.-B., (1999) Effect of elevated temperature curing on properties of alkali-activated slag concrete, Cement and Concrete Research 29, 1619–1625.
[11] Puertas F., Martínez-Ramírez S., Alonso S., Vázquez T., (2000) Alkali-activated fly ash/slag cements: strength behaviour and hydration products, Cement and Concrete Research 30, 1625–1632.
[12] ASTM C 109, (2016) Standard Test Method for Compressive Strength of Hydraulic Cement Mortars, ASTM International, West Conshohocken, United States.
[13] ASTM C 642, (2013) Standard Test Method for Density, Absorption, and Voids in Hardened Concrete, ASTM International, West Conshohocken, United States.
[14] Nath P., Sarker P.K., (2014) Effect of GGBFS on setting, workability and early strength properties of fly ash geopolymer concrete cured in ambient condition, Construction and Building Materials 66, 163–171.
[15] Gao, X., Yu, Q.L., Brouwers, H. J. H., (2015) Reaction kinetics, gel character and strength of ambient temperature cured alkali activated slag–fly ash blends, Construction and Building Materials 80, 105-115.
[16] Mastali M., Kinnunen P., Dalvand A., Mohammadi Firouz R., Illikainen M., (2018) Drying shrinkage in alkali-activated binders – A critical review, Construction and Building Materials 190, 533–550.
[17] Collins F., Sanjayan J., (2000) Effect of pore size distribution on drying shrinking of alkali-activated slag concrete, Cement and Concrete Research 30, 1401–1406.

Sigma Mühendislik ve Fen Bilimleri Dergisi-Cover

ISSN: 1304-7191
Yayın Aralığı: Yılda 4 Sayı
Yayıncı: Yıldız Teknik Üniversitesi

Arşiv