Mete Han BOZTEPE, Melih BAYRAMOĞLU, Çağrı UZAY, Necdet GEREN

Improving the Adhesion Bonding Strength for FML Composites by Using an Extremely Thin Mesh Steel

Fiber metal laminate (FML) is an advanced composite material that combine the advantageous of both fiber reinforced composites and metal alloys without sharing their individual disadvantages. When it is compared to commonly known fiber reinforced polymer composites, the FML provide better impact resistance and fatigue strength. But the production of a FML composite is a major problem since the bonding at fiber-metal interface can be poor. For this reason, the adhesion bonding capability at the fiber-metal interface was investigated in this study. Carbon fiber and glass fiber fabrics having both ±45° and 0°-90° orientation were used as fiber layers. And extremely thin stainless steel materials in the mesh form were used as metal layers. The mesh sizes of the layers are 100 and 500 respectively. The produced specimens having 12 different configurations were subjected to single lap shear tests according to ASTM D 5868-01 Standard. The results showed that 500-mesh stainless steel favorably affected the adhesion bonding strength.

Keywords:

Fiber metal laminate (FML), composites, mesh steel, single lap shear,

PDF

___

[1] Zhang P. Q., Ruan J. H., Li W. Z., (2001) “Influence of Some Factors on the Damping Property of Fiber-einforced Epoxy Composites at Low Temperature”, Cryogenics, vol.41, pp.245-253.
[2] Bhatnagar T., Ramakrishnan N., Kaik N. K., Komanduri R., (1995) “On the Machining of Fiber Reinforced lastic (FRP) Composite Laminates”, International Journal Mach. Tools Manufacture, vol. 35(5), pp.701-708.
[3] Botelhoa C. E., Silvac A. R., Pardinia C. L., Rezendea C. M., (2006) “A Review on the Development and Properties of Continuous Fiber/epoxy/aluminum Hybrid Composites for Aircraft Structures”, Materials Research, Vol. 9, No. 3, pp. 247-256.
[4] Calik A. and Yilidirm S., (2017) “Effect of adherend recessing on bi-adhesively bonded single-lap joints with spew fillet”, Sādhanā, Vol. 42, No. 3, pp. 317–325.
[5] Cortes P. and Cantwell W.J., (2006) “The prediction of tensile failure in titanium-based thermoplastic fibre–metal laminates”, Composites Science and Technology, vol. 66, pp. 2306–2316.
[6] Vogelesang L.B. and Vlot A., (2000) “Development of fibre metal laminates for advanced aerospace structures”, Journal of Materials Processing Technology, vol. 103, pp. 1-5.
[7] Khalili S.M.R., Daghigh V. and Farsani R.E., (2011) “Mechanical behavior of basalt fiber-reinforced and basalt fiber metal laminate composites under tensile and bending loads”, Journal of Reinforced Plastics and Composite, vol.30(8), pp. 647–659. DOI: 10.1177/0731684411398535
[8] Gonzalez-Canche N.G., Flores-Johnson E.A., Carrillo J.G., (2017) “Mechanical characterization of fiber metal laminate based on aramid fiber reinforced polypropylene”, Composıte Structures, Vol. 172, pp. 259-266. DOI: 10.1016/j.compstruct.2017.02.100
[9] Carrillo J.G. and Cantwell W.J., (2009) “Mechanical properties of a novel fiber–metal laminate based on a polypropylene composite”, Mechanics of Materials, Vol.41, pp.828–838. doi:10.1016/j.mechmat.2009.03.002.
[10] Calik A., (2016) “EFFECT OF ADHEREND SHAPE ON STRESS CONCENTRATION REDUCTION OF ADHESIVELY BONDED SINGLE LAP JOINT”, Engineering Review, Vol. 36, Issue 1, pp. 29-34

Yayın Aralığı: Yılda 4 Sayı
Başlangıç: 2017
Yayıncı: Ahmet Çalık

Arşiv