İhsan EFEOĞLU, Ayşenur KELEŞ, Göksel DURKAYA, Yaşar TOTİK, Kıvılcım ERSOY

Synthesis and investigation of structural-mechanical-tribological properties of c-BN based BN thin films

c-BN films are candidate material to diamond due to their promising properties. Although some properties of c-BN films are better than diamond, adhesion properties between the substrate and the film are very poor. In this study, c-BN films were deposited by closed-field unbalanced magnetron sputtering system onto 4140 steels in Ar/N2 atmosphere. The c-BN films coated in three different N2flow rates. The coated specimens were characterized by SEM and X-ray diffraction techniques. The bonding state of B, N and C elements were obtained using XPS. The mechanical properties of the c-BN films were tested by micro-indentation. The adhesion properties between substrate and the film were investigated by using scratch test. The tribological properties were carried out using pin-on-disc in atmospheric conditions. Our results showed that the c-BN films exhibited very dense and columnar microstructure. The maximum critical load was read 23 N in the softest c-BN film. The maximum and minimum hardness were measured 69 GPa and 33 GPa, respectively. When the hardness was increased the friction coefficient was decreased. The lowest friction coefficient (0.15) was obtained from the hardest film and the highest friction coefficient (0.65) was obtained from the lowest hardness

PDF

___

[1] Audronis M., Valiulis A. V., Silickas P., Recent Developments in the Deposition of c-BN Coatings, Mater. Sci. (Medziagotyra), 10, 152-156, 2004.
[2] Jimenez I., Torres R., Caretti I., Gago R., Albella J. M., A review of monolithic and multilayer coatings within the boron-carbon-nitrogen system by ion-beam-assisted deposition, J. Mater. Res., 27, 743-764, 2012.
[3] Zhang W. J., Chong Y. M., Bello I., Lee S. T., Nucleation, growth and characterization of cubic boron nitride (cBN) films, J. Phys. D: Appl. Phys., 40, 6159- 6174, 2007.
[4] Ma X. Y., Yue J. S., He D. Y., Chen G. G., Characterization of cubic boron nitride thin films grown on different substrates, Mater. Lett., 36, 206-209, 1998.
[5] Klett A., Freudenstein R., Kulisch W., Dependence of the stress of c-BN films on the major deposition parameters: Theoretical and experimental studies, Thin Solid Films, 398, 130-136, 2001.
[6] Ye J., Ulrich S., Zlebert C., Stuber M., Stress reduction of cubic boron nitride films by oxygen addition, Thin Solid Films, 517, 1151-1155, 2008.
[7] Ulrich S., Ye J. A., Stuber M., Influence of Ar-N-2 gas composition on the magnetron-sputter deposition of cubic boron nitride films, Surf. Coat. Technol., 205, S96-S98, 2010.
[8] Caicedo J. C., Caicedo H. H., Aperador W., TiN BCN/ BN (n)/c-BN system improves the surface properties of machining tools used in industrial applications, Int. J. Adv. Manuf. Technol., 77, 819-830, 2015.
[9] Teer D. G., Magnetron Sputter Ion Plating, U.S. Patent, 5,556,519, 1996.
[10] Cicek H., Baran O., Demirci E. E., Tahmasebian M., Totik Y., Efeoglu I., The effect of nitrogen flow rate on TiBN coatings deposited on cold work tool steel, J. Adhes. Sci. Technol., 28, 1140-1148, 2014.
[11] Fan X. H., Guo X. F., Xu B., ZhanG W., Cai L. C., Xray photoelectron spectroscopy research on superficial layer of cubic boron nitride crystals grown under HPHT High Temperatures-High Pressures, 44, 407-414, 2015.
[12] Gaitan G. B., Caicedo J. C., Prieto P., Balogh A. G., Cutting tool performance enhancement by using a B4C/BCN/C-BN multilayer system, Phys. Status Solidi C, 11, 4282-4287, 2007.
[13] Prakash A., Todi V., Sundaram K. B., Ross L., Xu G., French M., Henry P., King S. W., Investigation of the dielectric and mechanical properties for magnetron sputtered BCN thin films, ECS J. Solid State Sci. Technol., 4, N3122-N3126, 2014.
[14] Kiryukhantsev-Korneev P. V., Pierson J. F., Kuptsov K. A., Shtansky D. V, Hard Cr–Al–Si–B–(N) coatings deposited by reactive and non-reactive magnetron sputtering of CrAlSiB target Appl. Surf. Sci., 314, 104-111, 2014.
[15] Bowden F. P., Tabor D., The Friction and Lubricating of Solids, Oxford University Press, New York, 1950.