THE INFLUENCE OF POLYPYRROLE COATING ON CORROSION BEHAVIOR OF ZnNi DEPOSITED COPPER ELECTRODE
Bilayer and monolayer coatings offer good protection against metal and alloy corrosion. The protection of copper against corrosion via the use of metallic and polymeric coatings has been the subject of considerable research in the last decade. In this study, ZnNi plating was successfully deposited on the Cu electrode applying current of 7 mA with chronopotentiometry technique in the acidic solution. The PPy film was synthesized on thin ZnNi plating which deposited electrochemically on the copper surface. Homopolymer film was achieved using cyclic voltammetry technique in sodium oxalate solution containing pyrrole monomer. PPy coating provided a significant barrier property due to its lower permeability as well as the improvement the barrier behavior in time.
Anahtar Kelimeler:
Corrosion, Polypyrrole, Alloy, Copper, EIS
THE INFLUENCE OF POLYPYRROLE COATING ON CORROSION BEHAVIOR OF ZnNi DEPOSITED COPPER ELECTRODE
Bilayer and monolayer coatings offer good protection against metal and alloy corrosion. The protection of copper against corrosion via the use of metallic and polymeric coatings has been the subject of considerable research in the last decade. In this study, ZnNi plating was successfully deposited on the Cu electrode applying current of 7 mA with chronopotentiometry technique in the acidic solution. The PPy film was synthesized on thin ZnNi plating which deposited electrochemically on the copper surface. Homopolymer film was achieved using cyclic voltammetry technique in sodium oxalate solution containing pyrrole monomer. PPy coating provided a significant barrier property due to its lower permeability as well as the improvement the barrier behavior in time.
Keywords:
Corrosion, polypyrrole, alloy, copper,
___
- 1. Aal, A.A., (2007). Development of nickel coatings by TiN interlayer. Mater. Chem. Phys., 106, 317-322.
- 2. Ashassi-Sorkhabi H. and Rafizadeh, S.H., (2004). Effect of coating time and heat treatment on structures and corrosion characteristics of electroless Ni-P alloy deposits. Surf. Coat. Tech. 176, 318-326.
- 3. Sohi, M.H. and Jalali, M.J., (2003). Study of the corrosion properties of zinc-nickel alloy electrodeposits before and after chromating. Mater. Process. Tech. 138, 63-66.
- 4. Martins, J.I., Reis, T.C., Bazzaoui, M., Bazzaoui E.A., and Martins, L., (2004). Polypyrrole coatings as a treatment for zinc-coated steel surfaces against corrosion. Corr. Sci. 46, 2361-2381.
- 5. Özyılmaz, A.T., Kardaş, G., Erbil, M., Yazici, B., (2005). The corrosion performance of polyaniline on nickel plated mild steel. Appl. Surf. Sci. 242, 97-106.
- 6. Oren, Y., Landau, U., (1982). Growth of zinc dendrites in acidic zinc chloride solutions. Electrochim. Acta 27, 739-748.
- 7. Bajat, J.B., Miskovic-Stankovoc, V.B., Maksimovic, M.D., Drazic, D.M., Zec, S., (2002). Electrochemical deposition and characterization of ZnCo alloys and corrosion protection by electrodeposited epoxy coating on ZnCo alloy. Electrochim. Acta 47, 4101-4112.
- 8. Bajat, J.B., Mišković-Stanković, V.B., (2004). Protective properties of epoxy coatings electrodeposited on steel electrochemically modified by Zn–Ni alloy. Prog. Org. Coat. 49, 183-196.
- 9. Abou-Krisha, M.M., Assaf, F.H., El-Naby, S.A., (2009). Electrodeposition behavior of zic-nickel-iron alloys from sulfate bath. J. Coat. Technol. Res, 6(3), 391-399.
- 10. Hosking, N.C., Ström, M.A., Shipway, P.H., Rudd, C.D.,(2007). Corrosion resistance of zinc–magnesium coated steel. Corr. Sci. 49, 3669-3695.
- 11. Rajagopolan R. and Iroh, J.O., (2003). Characterization of polyaniline–polypyrrole composite coatings on low carbon steel: a XPS and infrared spectroscopy study. App. Surf. Sci. 218, 58-69.
- 12. Pawar, P., Sainkar, S.R., Patil, P.P., (2007). Synthesis of poly(aniline-co-o-toluidine) coatings and their corrosion-protection performance on low-carbon steel. J. Appl. Polym. Sci. 103(3), 1868-1878.
- 13. Olad, A. and Rasouli, H., (2010). Enhanced Corrosion Protective Coating Based on Conducting Polyaniline/Zinc Nanocomposite J. Appl. Polym. Sci. 115, 2221-2227.
- 14. Sazou, D., Kourouzidou, M., Pavlidou, E., (2007). Potentiodynamic and potentiostatic deposition of polyaniline on stainless steel: Electrochemical and structural studies for a potential application to corrosion control. Electrochim. Acta 52(13), 4385-4397.
- 15. Martyak, N.M., Mc Andrew, P., McCaskie J.E. and Dijon, D., (2002). Electrochemical polymerization of aniline from an oxalic acid medium. Prog. Org. Coat. 45, 23-32.
- 16. Wankhede, M.G., Gaikwad, A.B., Patil, P.P., (2006). Electrochemical polymerization of o-anisidine on low carbon steel from aqueous salicylate solution: Corrosion protection study. Surf. Coat. Tech. 201(6), 2240-2247.
- 17. Lu, H., Zhou, Y., Vongehr, S.,Hu, K., Meng, X., (2011). Electropolymerization of PANI coating in nitric acid for corrosion protection of 430 SS. Synthetic Metals 161(13-14), 1368-1376.
- 18. Mert, B.D., Solmaz, R., Kardas, G., Yazici, B., (2011). Copper/polypyrrole multilayer coating for 7075 aluminum alloy protection. Prog. Org. Coat. 72(4), 748-754.
- 19. Ozyilmaz A.T. and Akdag, A., (2011). Polyaniline, poly(N-methylaniline) and poly(aniline-co-N-methylaniline) coatings on stainless steel. Trans. MF. 89, 215-224.
- Başlangıç: 2009
- Yayıncı: E-Journal of New World Sciences Academy