Sürtünme karıştırma kaynağı ile birleştirilen magnezyum levhaların mekanik özelliklerinin incelenmesi

The use of magnesium, which is the latest metal of our age, is increasing in parallel with the advances in industry and technology. Due to its lightness, durability and long life, its usage is increasing in the automotive and space-craft industries. As a result of the advances in magnesium use, there are innovations in welding methods as well. The desired mechanical properties can't be obtained after welding. While there are some difficulties in fusion welding of magnesium material and its alloys, some of them can't be joined by fusion welding at all. Weldability of a material is the property that plays an important role in enabling its wider use and determines the method of producing products out of this material. Magnesium plates were joined successfully by friction stir welding method. Welded joints are exposed to various mechanic stresses and especially to dynamic loads. Cracks are observed to occur due to dynamic loads. Plates were joined in butt position and the mechanical properties of the occurring joint are examined.

Anahtar Kelimeler:

Magnezyum alaşımları, kaynak, sürtünme karıştırma kaynağı, eğme yorulması

Examination of mechanical properties of magnesium plates joined by friction stir welding

Keywords:

Magnesium alloys, welding, friction stir welding, bending fatigue,

PDF

___

ZEYTİN, H.K.; Magnezyum Alaşımları: Otomotiv Endüstrisinde Uygulaması ve Geleceği”, Marmara Araştırma Merkezi, Gebze Kocaeli, 1999
DAVIS. J, "The Potantial for Vehicle Weight Reduction Using Magnesium", SAE Technical Paper Series, International Congress and Exposition, Detroit, Michigan, 25 February-1 March, 1991
REINASS, G. Magnesiumguss, Werkstoffe und Werkstoffeigenschaften Giesserei, 79, Nr.21-26, s.903- 911, October 1992
BARNES, L.T, "Rolled Magnesium Products", 49th. Annual World Conference Magnesium, Chicago, Illıonis, USA, 7 Apr. 1994
DECKER. R. F., "The Renaissansce in Magnesium" Advanced Materials and Processes, 9, pp.(31-33), 1998
BERTZ, G; FUCHS A; ZEUMER, N." Neue Entwicklung beim Giessen von Magnesium", Gisserei, 75, Nr.8, s.246-250, April 1988
FROES, H. F., "The First International Conference on Magnesium Science and Technology", November 10- 12, Dead Sea, Israel, 1997
WELLS. P, NIEUWENHUIS. P, "Automotiv Materials", The Challenge ofGlobalisation and Technological Chance, Persians Professional Limited, Maple House 149 Tottenham Counrt Road, Londra WIP 9LL, 1998
SCHEMME, K, "Magnesiumwekstoffw für die neunziger Jahre", Alumınıum, 67. Jahrgang, 2, s.167- 179, 1991
OLSEN A.L, "Korrosioneigenschaften von neun Magnesiumlegierungen", Metall, 46.Jahrgang, Heft 6, s. 570-574, Juni 1992
HAWKE. D; OLSEN.A., "Corrosion Properties of New Magnesium Alloys", International Congress and Exposition, Detroit, Michigan, 1-5 March 1993
KAPLAN, H. " The Making of Magnesium", Light
Metal Age, s.18, June 1990
HERURTH. K; "High-Tech-Guss in der Anvendung- Sonderschau der GIFA 89, Magnesiumlegierungen", Gisserei 76, Nr. 15 S.482, Juli 1989
,[14]. BUSK, S.R, "Magnesium Products Design", International Magnesium Association, Marcel Dekker, Inc, New York Basel, 1986
ŞIK A., Sürtünme Karıştırma Kaynağı ile Birleştirilen Alimünyum Levhaların Eğme ve Yorulma Özelliklerinin İncelenmesi, SAÜ Fen Bilimleri Enstitüsü Dergisi Cilt: 9, Sayı: 2, 2005
ŞIK, A., “Otomobil Saclarının MIG/MAG kaynağında gaz karışımlarının bağlantının mekanik özelliklerine etkisi”, Gazi Üniversitesi Fen Bilimleri Enstitüsü Doktora Tezi, 2002
GÜLENÇ, B., “MIG/MAG kaynağında koruyucu gaz karışımının kaynak metalinin mekanik özelliklerine etkisi”, Gazi Üniversitesi Fen Bil. Enstitüsü, Doktora Tezi, Ankara, 1995
ŞIK, A., ERTÜRK İ. ve ÖNDER, M, “AA2024 alüminyum alaşımının sürtünme karıştırma kaynağında farklı parametrelerin mekanik özelliklere etkisinin incelenmesi” Pamukkale Üniversitesi Mühendislik Fakültesi, Cilt: 16, Sayı: 2, Sayfa: 141-150, 2010
ÇAM, G., “Sürtünme karıştırma kaynağı (SKK): al- alaşımları için geliştirilmiş yeni bir kaynak teknolojisi”, Mühendis ve Makina Cilt:46 Sayı:541, 2005
KULEKÇİ, M. K., ŞIK A., KALUÇ, E., “Effects of tool rotation and pin diameter on fatigue properties of friction stir welded lap joints” Int J Adv Manuf Technol, 36:877–882 DOI 10.1007/s00170-006-0901- z, 2008
GÜRLER, M., “Alüminyum alaşımlarının sürtünme kaynak özellikleri”, Doktora tezi, Marmara Üniversitesi Fen Bilimleri Enstitüsü, İstanbul, 2000
KULEKÇİ, M.K., ŞIK, A., “Effects of Tool Rotation and Transverse Speed on Fatigue Properties of Friction Stir Welded AA 1050-H18 Aluminium Alloy”, Archives of Metallurgy and Materials, 51/2, 213-218, 2006
BULUT, R., “Magnezyum AZ31 Alaşımının Sürtünme Karıştırma Kaynağı ile Birleştirilebilirliğinin İncelenmesi” Yüksek Lisans Tezi Makine Eğitimi Anabilim Dalı, Dumlupınar Üniversitesi Fen Bilimleri Enstitüsü, 2009
KAYABAŞ, Ö., “Sürtünme Karıştırma Kaynağı İle Yapılan Alüminyum Kaynağında Kaynak Bölgesinin Mekanik Özelliklerinin İncelenmesi”, Yüksek Lisans Dönem Projesi, Gazi Üniversitesi Fen Bilimleri Enstitüsü, Ankara 2005
KURT, A., ÖZDEMİR, M., BOZ, M., “Alüminyum Malzemelerin Sürtünme Karıştırma Kaynağında Kaynak Hızının Birleşebilirliğe Etkisi”, TMMOB Makine Mühendisleri Odası Kaynak Teknolojisi IV. Ulusal Kongre ve Sergisi, 89-99, Kocaeli 2003