Effect of Diffusion Annealing Temperature on Crack-initiating Omnipresent Flaws, Void/crack Propagation and Dislocation Movements Along Ni Surface-layered Bi-2223 Crystal Structure
Effect of Diffusion Annealing Temperature on Crack-initiating Omnipresent Flaws, Void/crack Propagation and Dislocation Movements Along Ni Surface-layered Bi-2223 Crystal Structure
Sakarya University Journal of Science
2018-Cilt: 22 Sayı: 5
1211-1220
Bi-2223 crystal structure,
Ni impurity diffusion,
annealing temperature,
cracks/voids,
dislocations