Compressive strength variation of alkali activated fly ash/slag concrete with different NaOH concentrations and sodium silicate to sodium hydroxide ratios
Compressive strength variation of alkali activated fly ash/slag concrete with different NaOH concentrations and sodium silicate to sodium hydroxide ratios
Waste disposal becomes a crucial issue for both the environment and the economy. One of the solutions for waste disposal is to utilize waste materials in concrete production. Nowadays, alkali activated concrete takes attention since waste materials (fly ash and ground granulated blast furnace slag) are utilized instead of ordinary Portland cement as binder materials. In this study, alkali activated fly ash/slag concrete is produced using 50% F-type fly ash and 50% ground granulated blast furnace slag and the compressive strength of the alkali activated fly ash/slag concrete is evaluated. The sodium silicate (Na 2SiO3) and sodium hydroxide (NaOH) solutions were utilized with four different sodium silicate to sodium hydroxide ratios (1, 1.5, 2, and 2.5) and three different molarities were utilized (6M, 10M, and 14M) for alkali activation to determine the effect of these parameters on the compressive strength of the alkali activated fly ash/slag concrete. In addition to ambient-curing (AC), the influence of the delayed oven-curing (OC) was also studied to determine the effect of curing regime on the compressive strength of the alkali activated fly ash/slag concrete. The results indicated that both the alkali activator ratio and NaOH concentration significantly affected the compressive strength of the alkali activated fly ash/slag concrete. In addition, the delayed oven-curing was also found as an important parameter for the compressive strength of the alkali activated fly ash/slag concrete.
___
- 1. Malhotra, V. M. (1999). Making concrete" greener" with fly ash. Concrete international, 21(5), 61-66.
2. Tho-In, T., Sata, V., Boonserm, K., and Chindaprasirt, P. (2018). Compressive strength and
microstructure analysis of geopolymer paste using waste glass powder and fly ash. Journal of Cleaner
Production, 172, 2892-2898.
3. Kurtoglu, A. E., Alzeebaree, R., Aljumaili, O., Nis, A., Gulsan, M. E., Humur, G., and Cevik, A. (2018).
Mechanical and durability properties of fly ash and slag based geopolymer concrete. Advances in
Concrete Construction, 6(4), 345–362.
4. Çevik, A., Alzeebaree, R., Humur, G., Niş, A., and Gülşan, M. E. (2018). Effect of nano-silica on the
chemical durability and mechanical performance of fly ash based geopolymer concrete. Ceramics
International, 44(11), 12253-12264.
5. Alzeebaree, R., Gulsan, M. E., Nis, A., Mohammedameen, A., and Cevik, A. (2018). Performance of
FRP confined and unconfined geopolymer concrete exposed to sulfate attacks. Steel and Composite
Structures, 29(2), 201-218.
6. Fernández-Jiménez, A., Palomo, J. G., and Puertas, F. (1999). Alkali-activated slag mortars: mechanical
strength behaviour. Cement and Concrete Research, 29(8), 1313-1321.
7. Somna, K., Jaturapitakkul, C., Kajitvichyanukul, P., and Chindaprasirt, P. (2011). NaOH-activated
ground fly ash geopolymer cured at ambient temperature. Fuel, 90(6), 2118-2124.
8. Saha, S., and Rajasekaran, C. (2017). Enhancement of the properties of fly ash based geopolymer paste
by incorporating ground granulated blast furnace slag. Construction and Building Materials, 146, 615-
620.
9. Singh, B., Rahman, M. R., Paswan, R., and Bhattacharyya, S. K. (2016). Effect of activator concentration
on the strength, ITZ and drying shrinkage of fly ash/slag geopolymer concrete. Construction and
Building Materials, 118, 171-179.
10. Fernandez-Jiminez A.M., Palomo A., Lopez-Hombrados C. (2006). Engineering properties of alkaliactivated fly ash concrete. ACI Mater. J. 103 (2) 106–112.
11. Hardjito D., Wallah S.E., Sumajouw M.J., Rangan B.V. (2004). On the development of fly ash-based
geopolymer concrete, ACI Mater. J. 101 (6) 467–472.
12. Diaz-Loya E.I., Allouche E.N., Vaidya S. (2011). Mechanical properties of fly ash-based geopolymer
concrete, ACI Mater. J. 108 (3) 300–306.
13. Sofi M., van Deventer J.S.J., Mendis P.A., Lukey G.C. (2007). Engineering properties of inorganic
polymer concretes, Cem. Concr. Res. 37 (2) 251–257.
14. Bakharev, T. (2005). Geopolymeric materials prepared using Class F fly ash and elevated temperature
curing. Cement and Concrete Research, 35(6), 1224-1232.
15. Lee, N. K., and Lee, H. K. (2013). Setting and mechanical properties of alkali-activated fly ash/slag
concrete manufactured at room temperature. Construction and Building Materials, 47, 1201-1209.
16. Phoo-ngernkham, T., Maegawa, A., Mishima, N., Hatanaka, S., and Chindaprasirt, P. (2015). Effects of
sodium hydroxide and sodium silicate solutions on compressive and shear bond strengths of FA–GBFS
geopolymer. Construction and Building Materials, 91, 1-8.
17. Hassan, A., Arif, M., and Shariq, M. (2019). Use of Geopolymer Concrete for a Cleaner and Sustainable
Environment–A Review of Mechanical Properties and Microstructure. Journal of Cleaner Production,
223, 704-728.
18. Hardjito D., Rangan B.V. (2005). Development and Properties of Low-calcium Fly Ash Based
Geopolymer Concrete, Australia Curtin University of Technology, Perth, p. 48.
19. Chindaprasirt, P., De Silva, P., Sagoe-Crentsil, K., and Hanjitsuwan, S. (2012). Effect of SiO2 and
Al2O3 on the setting and hardening of high calcium fly ash-based geopolymer systems. Journal of
Materials Science, 47(12), 4876-4883.
20. Leong, H. Y., Ong, D. E. L., Sanjayan, J. G., and Nazari, A. (2016). The effect of different Na2O and
K2O ratios of alkali activator on compressive strength of fly ash based-geopolymer. Construction and
Building Materials, 106, 500-511.
21. Singh, G. B., and Subramaniam, K. V. (2017). Evaluation of sodium content and sodium hydroxide
molarity on compressive strength of alkali activated low-calcium fly ash. Cement and Concrete
Composites, 81, 122-132.
22. Albitar, M., Ali, M. M., Visintin, P., and Drechsler, M. (2017) Durability evaluation of geopolymer and
conventional concretes, Construction and Building Materials, 136, 374-385.
23. Soutsos, M., Boyle, A. P., Vinai, R., Hadjierakleous, A., and Barnett, S. J. (2016) Factors influencing the
compressive strength of fly ash based geopolymers, Construction and Building Materials, 110, 355-368.
24. Temuujin, J. V., Van Riessen, A., and Williams, R. (2009). Influence of calcium compounds on the
mechanical properties of fly ash geopolymer pastes. Journal of hazardous materials, 167(1-3), 82-88.