UNPASSIVATED HIGH OPERATING TEMPERATURE GaInAsSb INFRARED PHOTODETECTOR GROWN ON GaAs SUBSTRATE

Ga0.87In0.13As0.4Sb0.96 photodiode structure was grown on semi-insulating 4” GaAs substrate by molecular beam epitaxy. The composition, crystal quality and dislocation density of epilayers were determined by high resolution X-ray diffraction rocking curve measurements. The threading dislocation density of the photodetector structure was calculated from the rotational broadening as ~2.5x108 cm-2. The cutoff wavelength and the peak responsivity of the photodetector were determined as around 2.15 μm and 0.08 A/W at 300 K, respectively. By applying reverse bias (-100 mV) the responsivity value of the photodetector increases more than an order (~0.96 A/W) which is the best value reported up to now. Those results indicate that although there is a large lattice mismatch (~8.4%) between GaAs substrate and the photodetector structure, an acceptable photodetector performance was achieved which is important for reducing photodetector costs.

Keywords:

MBE GaInAsSb, HRXRD, Photodetector,

PDF

___

Bergman L, McHale JL. Handbook of luminescent semiconductor materials. 1st ed. New York, CRC Press, 2011. pp.194.
Rogalski A. History of infrared detectors. Opto−Electronics Review 2012; 20: 279–308.
Downs C, Vandervelde TE. Progress in infrared photodetectors since 2000. Sensors (Basel) 2013; 13: 5054–5098.
Martyniuk P, Kopytko M, and Rogalski A. Barrier infrared detectors. Opto−Electronics Review 2014; 22: 127–146.
Gordon NT, Baker IM. Infrared detectors and emitters: materials and devices. 1st ed. United Kingdom: Springer, 2001. pp. 40.
Yildirim A, Prineas JP. Suppressed phase separation in thick GaInAsSb layers across the compositional range grown by molecular beam epitaxy for 1.7–4.9 μm infrared materials J Vac Sci Technol B 2012; 30: 02B104-1-7.
Nunna KC, Tan SL, Reyner CJ, Marshall ARJ, Liang B, Jallipalli A, David JPR, Huffaker DL. Short-wave infrared GaInAsSb photodiodes grown on GaAs substrate by interfacial misﬁt array technique. IEEE Photonics Tech L 2012; 24: 218-220.
Wang CA, Choi HK, Oakley DC, Charache GW. Recent progress in GaInAsSb thermophotovoltaics grown by organometallic vapor-phase epitaxy. J Cryst Growth 1998; 195, 346-355.
Lei L, Li L, Lotfi H, Jiang Y, Yang RQ, Johnson MB, Lubyshev D, Qiu Y, Fastenau JM, Liu AWK. Mid-wave interband cascade infrared photodetectors based on GaInAsSb absorbers. Semicond Sci Technol 2016; 31: 105014-1-7.
Reddy MHM, Olesberg JT, Cao C, Prineas JP. MBE-grown high-efficiency GaInAsSb mid-infrared detectors operating under back illumination. Semicond. Sci Technol 2006; 21: 267–272.
Bracker AS, Yang MJ, Bennett BR, Culbertson JC, Moore WJ. Surface reconstruction phase diagrams for InAs, AlSb and GaSb. J Cryst Growth 2000; 220: 384–392.
Erkus M, Senel O and Serincan U. Structural, optical and electrical characterization of InAs0.83Sb0.17 p-π-n photodetector grown on GaAs substrate. Thin Solid Films 2016; 616: 141–144.
Deng HY, Hong XK, Fang WZ, Dai N. Microstructure characterization of InAs0.93Sb0.07 films grown by ramp-cooled liquid phase epitaxy. Mater Charact 2007; 58: 307-311.
Ayers JE. The measurement of threading dislocation densities in semiconductor crystals by X-ray diffraction. J Cryst Growth 1994; 135: 71-77.
Wang G, Loo R, Simoen E, Souriau L, Caymax M, Heyns MM, Blanpain B. A model of threading dislocation density in strain-relaxed Ge and GaAs epitaxial films on Si (100). Appl Phys Lett 2009; 94: 102115-1-3.
Rogalski A. HgCdTe infrared detector material: history, status and outlook. Rep Prog Phys 2005, 68, 2267–2336.
Varshni YP. Temperature dependence of the energy gap in semiconductors. Physica 1967; 34: 149-154.

Eskişehir Technical University Journal of Science and Technology A - Applied Sciences and Engineering-Cover

ISSN: 2667-4211
Yayın Aralığı: Yılda 4 Sayı
Başlangıç: 2000
Yayıncı: Eskişehir Teknik Üniversitesi

Arşiv