Rahim ÖZGÜN, Ercan KÖSE, Mustafa Kemal KÜLEKÇİ, Uğur EŞME, Şeref ÖCALIR

Yüksek Isı Ortamının Otomat Çeliklerinin Yorulma Ömrüne Etkisinin İncelenmesi

Bu çalışmada yüksek ısı ortamının otomat çeliklerinin yorulma ömrüne etkisi incelenmiştir. Bu amaçla

Anahtar Kelimeler:

Yorulma testi, Otomat çeliği, Mikro denetleyici

An Investigation of Effect of High Temperature Environmental to Fatigue Life of Cutting Steels

In this study, effects of high temperature environmental to fatigue life have been investigated in cutting steels. For this purpose, fatigue testing machine of micro controller was designed for cylindrical material. The samples which were produced from cutting steels had been kept in high temperature (900 ºC) for 3 hours. Effects of high temperature to fatigue life have been investigated by exposing the samples kept and non-kept in high temperature to fatigue test for different tensiles in designed and produced machine. As result of experiments, it has been observed that the high temperature environment has reduced fatigue resistance in cutting steels. Besides, it was determined that pore intensity of samples kept in high temperature environment increased when the photographs taken from scanning electron microscope (SEM) were investigated.

Keywords:

Fatigue test, Cutting steel, Micro controller,

PDF

___

1. Yılmaz, S.S., Ünlü, B.S., Varol, R., 2007. Borlamanın Demir Esaslı T/M Malzemelerde Yorulma Davranışına Etkisi, Celal Bayar Üniversitesi Fen Bilimleri Dergisi, 3(1), 1-3.
2. Bhushan, B., Gupta, 1991. B.K., Handbook of Tribology, McGraw-Hill Inc., USA.
3. Black, J.T., Kohser, R.A., 2007. Materials and Process in Manufacturing, John Wiley & Sons.
4. Kalpakjian, S., 2001. Manufacturing Engineering and Technology, Addison Wesley, USA.
5. Groover, M. P., 2007. Fundamentals of Modern Manufacturing, John Wiley & Sons, USA.
6. McKelvey, S.A., Fatemi, A., 2011. Surface Finish Effect on Fatigue Behaviour of Forged Steel, International Journal of Fatigue, 36(1), 130-145.
7. Suh, C.M., Suh, M. S., Hwang N.S., 2012. Growth Behaviour of Small Surface Fatigue Cracks in AISI 304 Stainless Steel, Fatigue & Fracture of Engineering Materials & Structures, 35(1), 22-29.
8. Şengül, A. B., Çelik, A., 2012. Farklı Çevrim Sayılarında Uygulanan Aşırı Yüklemenin Oluşturduğu Yorulma Çatlak İlerleme Gecikmesi Üzerinde Plazma Nitrürlemenin Etkisi, Gazi Üniversitesi Mühendislik-Mimarlık Fakültesi Dergisi, 27(4), 707-715.
9. Jin, O., 2000. The Characterization of Small Fatigue Crack Growth in PH13-8 Molybdenum Stainless Steel, Doktora Tezi, Georgia University, Instuty of Technology.
10. Aviles, R., Albizuri, J., Lamikiz, A., 2011. Influence of Laser Polishing on the High Cycle Fatigue Strength of Medium Carbon AISI 1045 Steel, International Journal of Fatigue, 33(11), 1477-1489.
11. Shen, H., Guo, W., 2011. 3D Fracture Mechanichs Investigation Surface Fatigue Crack Propagation, Fatigue & Fracture of Engineering Materials & Structures, 34(9), 682-688.
12. Saygın, M., 2006. AISI 1020 Çeliklerinde Borlamanın Yorulma Dayanımına Etkisi, Yüksek Lisans Tezi, Osman Gazi Üniversitesi, Fen Bilimleri Enstitüsü.
13. Yaşar, M., 2007. Dizel Otomobil Pompa Milinin Yorulma Kırılması Analizi, 8. Uluslararası Kırılma Konferansı Bildiriler Kitabı, İstanbul, 544-553, 7-9 Kasım.
14. Gönen, D., Oral, A., Çakır, M. C., 2008. Çift Sıkıştırma Oranlı Yay Yorulma Test CihazıTasarım ve İmalatı, Balıkesir Üniversitesi Fen Bilimleri Enstitüsü Dergisi, 10(1), 98-108.
15. Türk Standartlar Enstitüsü, 2002. Metaller-Dönen Çubuk Eğme Yorulma Deneyleri, TS ISO 1143, Ankara.
16. Türk Standartları Enstitüsü, 2011. Metalik Malzemeler -Çekme Deneyi- Bölüm 1: Oda Sıcaklığında Deney Metodu, TS EN ISO 6892- 1, Ankara.