Effect of NaOCl solution on the cyclic fatigue resistance of traditional and heat-treated file systems
Effect of NaOCl solution on the cyclic fatigue resistance of traditional and heat-treated file systems
Aim: To compare the cyclic fatigue resistance at distilled water and %5.25 NaOCl of immersed ProTaper Gold (Dentsply Sirona,Ballaigues, Switzerland) and ProTaper Universal (Dentsply Sirona, Ballaigues, Switzerland) file systems.Material and Methods: The ProTaper Gold F2 (25.06v taper) and ProTaper Universal F2 (25.06v taper) file systems were immersedin distilled water andNaOCl for 5 minutes. After immersion process files were rotated at artificial canal with 60O curvature and a5-mm radius until fracture occurred. Time to fracture and fractured lengths were recorded. Data were analyzed statistically usingindependent t-tests. Statistical significance was set at P
___
- 1. Cheung GS, Liu CS. A retrospective study of endodontic
treatment outcome between nickel titanium rotary and
stainless steel hand filing techniques. J Endod 2009;35:938-
43.
- 2. Iqbal MK, Kohli MR, Kim JS. A retrospective clinical study
of incidence of root canal instrument separation in an
endodontics graduate program: a PennEndo database
study. J Endod 2006;32:1048-52.
- 3. Sattapan B, Nervo GJ, Palamara JE, et al. Defects in rotary
nickel-titanium files after clinical use. J Endod 2000;26:161-
5.
- 4. Shen Y, Zhou H-m, Zheng Y-f, et al. Current challenges and
concepts of the thermomechanical treatment of nickeltitanium
instruments. J Endod 2013;39:163-72.
- 5. Gutmann J, Gao Y. Alteration in the inherent metallic and
surface properties of nickel–titanium root canal instruments
to enhance performance, durability and safety: a focused
review. Int Endod J 2012;45:113-28.
- 6. Gambarini G, Grande NM, Plotino G, et al. Fatigue resistance of
engine-driven rotary nickel-titanium instruments produced
by new manufacturing methods. J Endod 2008;34:1003-5.
- 7. Bardsley S, Peters CI, Peters OA. The effect of three rotational
speed settings on torque and apical force with vortex rotary
instruments in vitro. J Endod 2011;37:860-4.
- 8. Hieawy A, Haapasalo M, Zhou H, et al. Phase Transformation
Behavior and Resistance to Bending and Cyclic Fatigue of
ProTaper Gold and ProTaper Universal Instruments. J Endod
2015;41:1134-8.
- 9. Clarkson RM, Moule AJ. Sodium hypochlorite and its use as
an endodontic irrigant. Aust Dent J 1998;43:250-6.
- 10. Mohammadi Z. Sodium hypochlorite in endodontics: an
update review. Int Dent J 2008;58:329-41.
- 11. Busslinger A, Sener B, Barbakow F. Effects of sodium
hypochlorite on nickel-titanium Lightspeed instruments. Int
Endod J 1998;31:290-4.
- 12. Berutti E, Angelini E, Rigolone M, et al. Influence of sodium
hypochlorite on fracture properties and corrosion of
ProTaper Rotary instruments. Int Endod J 2006;39:693-9.
- 13. O’hoy P, Messer H, Palamara J. The effect of cleaning
procedures on fracture properties and corrosion of NiTi
files. Int Endod J 2003;36:724-32.
- 14. Pedullà E, Grande NM, Plotino G, et al. Cyclic fatigue
resistance of three different nickel-titanium instruments
after immersion in sodium hypochlorite. J Endod
2011;37:1139-42.
- 15. Keles A, Ozyurek EU, Uyanik MO, et al. Effect of Temperature
of Sodium Hypochlorite on Cyclic Fatigue Resistance of
Heat-treated Reciprocating Files. J Endod 2019; 45: 205-8.
- 16. 16. Cardoso RM, Carvalho AN, Batista S, et al. Influence
of Temperature on the Cyclic Fatigue of Nickel-Titanium
Instruments with Different Heat Treatments on Severely
Curved Canals. J Contemp Dent Pract 2019;20:697-701.
- 17. Zinelis S, Darabara M, Takase T, et al. The effect of thermal
treatment on the resistance of nickel-titanium rotary files
in cyclic fatigue. Oral Surg Oral Med Oral Pathol Oral Radiol
Endod 2007;103:843-7.
- 18. Retamozo B, Shabahang S, Johnson N, et al. Minimum
contact time and concentration of sodium hypochlorite
required to eliminate Enterococcus faecalis. J Endod
2010;36:520-3.
- 19. Uygun A, Kol E, Topcu M, et al. Variations in cyclic fatigue
resistance among ProTaper Gold, ProTaper Next and
ProTaper Universal instruments at different levels. Int Endod
J 2016;49:494-9.
- 20. Plotino G, Grande NM, Bellido MM, et al. Influence of
temperature on cyclic fatigue resistance of ProTaper Gold
and ProTaper Universal rotary files. J Endod 2017;43:200-2.
- 21. Haapasalo M, Shen Y, Qian W, et al. Irrigation in endodontics.
Dental Clinics 2010;54:291-312.
- 22. Haapasalo H, Siren E, Waltimo T, et al. Inactivation of local
root canal medicaments by dentine: an in vitro study. Int
Endod J 2000;33:126-31.
- 23. Davis JR. Metals Handbook: Desk Edition. 2nd Edition. CRC
Press, Ohio, 1998;147-8.