Betonda Silis Dumanı ve Polipropilen Lif Kullanımının Beton Özellikleri Üzerine Etkilerinin İncelenmesi

target, the effect of alkali-silica reaction and sulfate provides many benefits like getting under control. Optimum silica fumes may be added to concrete, high strength and low heat in the hidratasyon destination, alkali silica reaction and to provide permeability under control provides many benefits such as receiving the effect of sulfate. Search surface area silica fumes contribution aggregates-paste without spaces and more than high strength concretes. However, there are also negative effects such as silica exposure by being streamed. The amount of the relative values of these effects optimum silica smoke and cement, aggregates, is determined based on the type and quantities such as the terms of maintenance with plasticizer additive factors are also affected. Polymer fibers, giving the best results and to participating in, and the most widely used polypropylene fiber blends. Polypropylene fiber concrete in three dimensions by creating a micro accessory network, reduce the deficit and the presence of natural concrete to be pumped some properties. In this study, exposure to silica, which is a waste material in theindustrial field on theproperties of concrete betonunda and silica exposure by joining concrete to improve the effects of the adverse effects on properties of polypropylene fiberconcrete.Keywords: Concrete Technology, Industrial Waste, Silica Fume, Polypropylene Fibers.

Anahtar Kelimeler:

Beton teknolojisi, Endüstriyel Atık, Silis Dumanı, Polipropilen Lif.

Investigation of polypropylene fiber effect to the silica fume concrete

Some of the characteristics of concretes of a variety of mineral additives to improve and participate in threads.The optimum amount of heat of hydration to reduce the addition of silica fume concrete, high strength and low permeability to provide the target, the effect of alkali-silica reaction and sulfate provides many benefits like getting under control. Optimum silica fumes may be added to concrete, high strength and low heat in the hidratasyon destination, alkali silica reaction and to provide permeability under control provides many benefits such as receiving the effect of sulfate. Search surface area silica fumes contribution aggregates-paste without spaces and more than high strength concretes. However, there are also negative effects such as silica exposure by being streamed. The amount of the relative values of these effects optimum silica smoke and cement, aggregates, is determined based on the type and quantities such as the terms of maintenance with plasticizer additive factors are also affected. Polymer fibers, giving the best results and to participating in, and the most widely used polypropylene fiber blends. Polypropylene fiber concrete in three dimensions by creating a micro accessory network, reduce the deficit and the presence of natural concrete to be pumped some properties. In this study, exposure to silica, which is a waste material in theindustrial field on theproperties of concrete betonunda and silica exposure by joining concrete to improve the effects of the adverse effects on properties of polypropylene fiberconcrete.

Keywords:

Concrete Technology, Industrial Waste, Silica Fume, Polypropylene Fibers.,

PDF

___

(REFERENCES) Çelik, Ö., “Uçucu Kül, Silis Dumanı Ve Atık Çamur Katkılarının Çimento Dayanımlarına Etkileri” Beton 2004 Hazır Beton Kongresi Bildiriler Kitabı.
Yeğinobalı A, 1993. Silis Dumanının Betonda Katkı Maddesi Olarak Değerlendirilmesi. Endüstriyel Atıkların İnşaat Sektöründe Kullanılması Sempozyumu
Bildirileri, Ankara, S.149-167. Özbek, R., 1998. Silis Dumanın Betonun Fiziksel Ve Mekanik Özelliklerine Etkisi, Gaziüniversitesi Fen Bilimleri Enstitüsü, Yüksek Lisans Tezi, Ankara, 86s.
Erbaş, M. (2003) Polipropilen Lifler Ve Betonun Dürabilitesine Etkisi., 5. Ulusal
Beton Kongresi, Mmo Yayınları, İstanbul, S.82 Erdoğan, T.Y.(2003), Beton, Odtü Geliştirme Vakfı Yayıncılık Ve İletisim A.S., Ankara. 54 S.
Türker, S., Balanlı, A., (1992).Yapı Malzemeleri, Yıldız Teknik Üniversitesi, İstanbul, S. 45-72.
Temiz, H. Ve Yeğinobalı, A.,1995. "Uçucu Kül Ve Silis Dumanı Katkılı Çimento Hamur Ve Harçlarının Bazı Özellikleri", Endüstriyel Atıkların İnşaat Sektöründe Kullanılması Sempozyumu, Bildiriler Kitabı, 213-226, İmo, Ankara.
Yetgin, Ş. Ve Çavdar, A., 2005, Doğal Puzolan Katkı Oranının Çimentonun Dayanım, İşlenebilirlik, Katılaşma Ve Hacim Genleşmesi
Özelliklerine Etkisi, Fırat Üniv. Fen Ve Müh. Bil. Der.,17 (4): 687-692. Arslan, A. Ve Aydın A.C., 1999, Lifli Betonların Genel Özellikleri, Hazır Beton Dergisi, (36): 67
Yıldırım, S.T., 2002. Lif Takviyeli Betonların Performans Özelliklerininaraştırılması. Fırat Üniversitesi Fen Bilimleri Enstitüsü, Doktora Tezi,Elazığ, 193s.
Ünal, B., Köksal, F., Eyyubov, C, 2003. Polipropilen Ve Çelik Liflerindonma Çözülme Ve Aşınma Dirençlerine Ortak Etkisi. 5. Ulusal Betonkongresi, Betonun Dayanıklılığı, İstanbul, S.345-354.
Ünal, B., 2003. Çelik Tel Ve Polipropilen Lif İçerikli Beton Yolların Mekanikselözelliklerinin Araştırılması. Erciyes Üniversitesi Fen Bilimleri Enstitüsü,Yüksek Lisans Tezi, Kayseri, 71s.
Uyan, M., 1985. Lifli Betonların Genel Özellikleri Ve Gelişimi. İtüinşaatfakültesi Malzeme Semineri, İstanbul, S.121-132.