Evaluation of color stability of bulk-fill restorative materials with different properties

Aims: The present study aims to evaluate the color stability of bulk-fill restorative materials with different properties over different time periods when immersed in a coffee solution. Methods: According to the selected restorative materials, the study groups were formed as follows: CNT/light (Alkasite, Cention N, Ivoclar Vivadent, light cure mode), CNT/self (Alkasite, Cention N, self cure mode) EQF (Glass hybrid restorative, Equia Forte HT, GC Corporation), AU (Single-shade bulk fill, Aura Bulk Fill, SDI), Z550 (Filtek Z550, 3M) (control group). A total of 50 samples (n=10) were prepared using standard molds (2mmx10mm). After finishing and polishing procedures, all samples were kept in distilled water at 37°C for 24 hours. The first color measurement (L*a*b ) was performed with Vita Easy Shade V (VITA Zahnfabrik). Samples were added to the coffee solution. Color was measured at times simulating 7 days, 1 month, 6 months and 1 year of clinical service. Color changes (ΔE1, ΔE2, ΔE3 and ΔE4) were calculated according to the CIE L*a*b system. Normality of the data was examined by D'Agostino & Pearson omnibus normality test. One-way ANOVA analysis and Tukey test were performed. Statistical significance level was set at p 0.05 and statistical analysis software (GraphPad Prism 6.0, GraphPad Software, USA) was used for the analysis. Results: According to ΔE1 results; clinically unacceptable color change (ΔE>3.3) values were observed in CNT/light and CNT/self groups. The color change values of EQF, Z550 and AU groups were statistically similar (p>0.05). According to ΔE2 results; an unacceptable color change (ΔE>3.3) was observed in all groups except EQF. According to ΔE3 results; an unacceptable color change (ΔE>3.3) was observed in all groups. According to ΔE4 results; an unacceptable color change (ΔE>3.3) was observed in all groups. The color change values of EQF, Z550 and AU groups were statistically similar (p>0.05). CNT/light group showed the highest color change in all time periods, followed by CNT/self group. Conclusion: The color stability of single-shade bulk fill material and glass hybrid restorative materials is similar to the control group. The color stability of alkasite material needs to be improved.

Keywords:

Alkasite, Bulk fill Cention N, Color Stability, Glass Hybrid,

PDF

___

Barutcigil Ç, Barutcigil K, Özarslan MM, Dündar A, Yilmaz B. Color of bulk-fill composite resin restorative materials. J Esthet Restor Dent. 2018;30(2):E3-E8.
Lucena C, Ruiz-López J, Pulgar R, Della Bona A, Pérez MM. Optical behavior of one-shaded resin-based composites. Dent Mater. 2021;37(5):840-848.
Paolone G, Mandurino M, Scotti N, Cantatore G, Blatz MB. Color stability of bulk-fill compared to conventional resin-based composites: a scoping review. J Esthet Restor Dent. 2023;35(4):657-676.
Veloso SRM, Lemos CAA, de Moraes SLD, do Egito Vasconcelos BC, Pellizzer EP, de Melo Monteiro GQ. Clinical performance of bulk-fill and conventional resin composite restorations in posterior teeth: a systematic review and meta-analysis. Clin Oral Investig. 2019;23(1):221-233.
Yazkan B. Surface degradation evaluation of different self-adhesive restorative materials after prolonged energy drinks exposure. J Esthet Restor Dent. 2020;32(7):707-714.
Latta MA, Tsujimoto A, Takamizawa T, Barkmeier WW. Enamel and dentin bond durability of self-adhesive restorative materials. J Adhes Dent. 2020;22(1):99-105.
Latta MA, Tsujimoto A, Takamizawa T, Barkmeier WW. In vitro wear resistance of self-adhesive restorative materials. J Adhes Dent. 2020;22(1):59-64.
Kaptan A, Oznurhan F, Candan M. In vitro comparison of surface roughness, flexural, and microtensile strength of various glass-ionomer-based materials and a new alkasite restorative material. Polymers. 2023;15(3):650.
Yazkan B, Celik EU, Recen D. Effect of aging on surface roughness and color stability of a novel alkasite in comparison with current direct restorative materials. Oper Dent. 2021;46(5):E240-E250.
Brkanović S, Ivanišević A, Miletić I, Mezdić D, Jukić Krmek S. Effect of nano-filled protective coating and different pH enviroment on wear resistance of new glass hybrid restorative material. Materials. 2021;14(4):755.
Gowda A, Guria A. Comparative evaluation of microleakage in alkasite and glass-hybrid restorative system: an in-vitro. IJRG 2019;7(4):199-205.
Güner ZŞ, Bolgül B, İnandı T. Evaluation of the color stability and surface roughness of dual-cure, bulk-fill composites. Int Dent Res. 2021;11(Suppl. 1):266-273.
Veček NN, Par M, Sever EK, Miletić I, Krmek SJ. The effect of a green smoothie on microhardness, profile roughness and color change of dental restorative materials. Polymers. 2022;14(10):2067.
Tepe H, Erdılek AD, Sahın M, Efes BG, Yaman BC. Effect of different polishing systems and speeds on the surface roughness of resin composites. J Conserv Dent JCD. 2023;26(1):36.
Ertas E, Gueler AU, Yuecel AC, Köprülü H, Güler E. Color stability of resin composites after immersion in different drinks. Dent Mater J. 2006;25(2):371-376.
Paolone G, Formiga S, De Palma F, et al. Color stability of resin-based composites: Staining procedures with liquids-a narrative review. J Esthet Restor Dent. 2022;34(6):865-887.
Korkut B, Haciali C. Color stability of flowable composites in different viscosities. Clin Exp Health Sci. 2020;10(4):454-461.
Meshki R, Rashidi M. Effect of natural and commercially produced juices on colour stability of microhybrid and nanohybrid composites. BDJ Open. 2022;8(1):11.
Hatirli H, Tonga G, Boyraz Ş. Water sorption, solubility and color stability of different bulk-fill restorative materials. Cumhur Dent J. 2022;25(4):293-301.
Barutcigil Ç, Yıldız M. Intrinsic and extrinsic discoloration of dimethacrylate and silorane based composites. J Dent. 2012;40:e57-e63.
Amalavathy RK, Sahoo HS, Shivanna S, Lingaraj J, Aravinthan S. Staining effect of various beverages on and surface nano-hardness of a resin coated and a non-coated fluoride releasing tooth-coloured restorative material: An in-vitro study. Heliyon. 2020;6(6):e04345