MİKROLİF TEKSTİL MALZEMESİNİN TEKSTİL MİMARİSİNDE KULLANILABİLİRLİĞİ - UV ABSORBANLARIN MALZEME ÇEKME DAYANIMINA ETKİSİ

Recently, new alternative materials are participated by the production of composites which includes polymer fibers. The fibers in the form of “Technical Textiles” show variety and provide spreading the modern structure systems in “Textile Architecture”. The fibers used in textile architectures are mainly polyester, polypropylene and polyamide fibers. Especially the fibers in the form of microfibers come forward because of the endurance against the climatic conditions. Microfiber textile surfaces has the air and water vapour permeability which is demanded for exterior coating, can also be used as exterior surface material when durability conditions were provided. In this research, the tensile strength of polyester microfiber material, used in textile industry, was researched under external conditions. Among these external conditions, especially UV radiation was an effective factor on the material surface. Due to this factor, different concentrations of UV absorbers were applied on microfiber. Undyed microfiber textile material was treated with 0%, 1%, 2%, 3% and 4% UV absorber concentrations. UV radiation of daylight was limited in 300-400 nm and material was exposed to accelerated aging experiment for 320 hours, which was equivalent to blue wool 7-l8 degree reference. The experimental results showed that UV absorber has a positive effect on aged material; however, concentration percentage differences do not provide any annex to endurance of material

Anahtar Kelimeler:

Microfiber, Aging experiment, UV absorber, Tensile strength, Textile architecture

THE AVAILABILITY OF MICROFIBER TEXTILE MATERIAL IN THE TEXTILE ARCHITECTURE - THE EFFECT OF UV ABSORBER ON MATERIAL TENSILE STRENGTH

Günümüzde, yapı malzeme gruplarına polimer lifler içeren kompozitlerin üretilmesiyle yeni alternatifler katılmıştır. Çeşitlilik gösteren bu lifler “Teknik Tekstiller” şeklinde, “Tekstil Mimarisinde” çağdaş strüktür sistemlerinin hızla yayılmasını sağlamıştır. Tekstil mimarisinde kullanılan lifler ağırlıklı olarak polyester, polipropilen ve poliamid liflerdir. Bu lifler arasında, özellikle mikrolif şeklinde olanlar iklim koşullarına karşı dayanıklılık göstermeleri nedeniyle öne çıkmaktadır. Mikrolif tekstil yüzeyleri hava ve su buharı geçirgenliğine sahipken, dış yüzey malzemesinden istenen dayanıklılık koşullarını sağlamaktadır. Bu araştırmada, tekstil sektöründe kullanılan polyester mikrolif malzemenin dış ortam koşullarına maruz kaldıktan sonra çekme dayanımı gibi mekanik özellikleri araştırılmıştır. Dış ortam koşulları arasında, özellikle UV radyasyon faktörü malzeme yüzeyinde etkili olmaktadır. Bu nedenle, farklı konsantrasyonlarda UV absorbanlar, mikrolif tekstil üzerine uygulanmıştır. Boyanmamış mikrolif tekstil malzemesi %0, %1, %2, %3 ve %4 UV absorban konsantrasyonları ile işlemden geçirilmiştir. Numuneler, gün ışığı ve UV radyasyonu 300-400 nm ile sınırlandırılarak, mavi yün 7-L8 derece referansa eşdeğer olacak şekilde 320 saat hızlandırılmış yaşlanma deneylerine maruz bırakılmıştır. Deney sonuçları incelendiğinde; UV absorbanın malzeme üzerinde olumlu etkisi olduğu; ancak, farklı konsantrasyon yüzdelerinin malzemenin dayanıklılığı üzerinde herhangi bir etkisinin olmadığı tespit edilmiştir

Keywords:

Mikrolif, Yaşlanma deneyi, UV absorban, Çekme dayanımı, Tekstil mimarisi,

PDF

___

1. Mecit D., Ilgaz S., Duran D., 2007, “Technical Textiles and Applications (Part 1)”, Tekstil ve Konfeksiyon, April-June, 17 (3), pp.79-82.
2. Eric M., 2002, Yapı Fiziği ve Malzemesi, Literatur Publisher , Istanbul. pp.157.
3. Perincek S.D., Duran K., Körlü A.E., 2007, “Ultraviyole Teknolojisi”, Tekstil ve Konfeksiyon, October- December, 17 (4), pp.219-223.
4. Demir A., Oktem T., Seventekin N., 2008, “The Effect of UV Absorbers on Light Fastness of Reactive Dyed Cotton Fabrics”, Tekstil ve Konfeksiyon, July- September, 18 (3), pp.211-22.
5. Rupp J., Bohringer A., Yonenaga A., 2001, “Textiles for Protection against Harmful Ultraviolet Radiation”, International Textile Bulletin, 47 (6) pp. 8 -20.
6. Reinert G., Schmidt E., Hilfiker R., 1994, “Facts about the Application of UV Absorbers on Textil”, Melliand Textilberiche 7-8, E, pp. 151-163.
7. Teichmann R., Vogel C., 1999, “Sun Protection Finishes”, Melliand International, 11, pp.320.
8. Alves M., Arruda C., Ogliari P., 2005, “Effect Of The Addition Of Ultraviolet Absorber (Tinuvin 234) on the quality of Soybean Oil Packaged In Polyethylene Terephthalate (PET)”, Grasasy Aceites 56 (4), pp. 245-253.
9. Paluszkiewicz J., Czajkowski W., Kazmierska M., 2005, “Reactive Dyes For Cellulose Fibres Including UV Absorbers”, Fibres & Textiles in Eastern Europe 13 (2), pp.76-80.
10. Tsatsaroni E. G., Eleftheriadis I. C., 2004, “UV-Absorbers In The Dyeing Of Polyester With Disperse Dyes”, Dyes and Pigments 61 (2), pp.141-147.
11. Wetz F., Routaboul, C., Denis, A. 2005, “A New Long-Chain UV Absorber Derived From 4-Tert-Butyl-4'-Methoxydibenzoylmethane: Absorbance Stability Under Solar Irradiation”, Journal of Cosmetic Science 56 (2), pp.135-148.
12. Thanki P. N., Singh, R., P., 2002, “Photostabilization Of Nylon 66 In Presence Of Acid Blue Dyes”, Polymer Degradation and Stability 75 (3), pp.423-430.
13. Fechine G.M., Rabello M.S., Maior R.S., 2004, “Surface Characterization Of Photodegraded Poly (Ethylene Terephthalate). The Effect of Ultraviolet Absorbers”, Polymer 45 (7), pp.2303-2308.
14. Pickett J.E., 2004, “UV Absorber Permanence and Coating Lifetimes”, Journal of Testing and Evaluation 32 (3), pp.240-245.
15. Lopez J.L., Sain, M., Cooper, P. 2006, “Performance of Natural-Fiber-Plastic Composites Under Stress For Outdoor Applications: Effect Of Moisture, Temperature, And Ultraviolet Light Exposure”, Journal of Applied Polymer Science 99 (5), pp.2570-2577.
16. Maishe, C., Elango, S., 2004, “Substituted Benzotriazole As UV Absorber For Paints”, Surface Coatings International Part B-Coatings Transactions 87 (4), pp.277-284.
17. Gorensek, M., Sluga, F., 2004, “Modifying The UV Blocking Effect Of Polyester Fabric”, Textile Research Journal 74 (6), pp.469-474.
18. Gezer, H., Merdan, N., 2006, “The Research of the Effect of UV Absorbents to the Tensile Strength in Usability of Colourless Microfiber Textile Materials in Outside Surfaces”, III. National Building Material Congress, Istanbul, pp.144-155.
19. Schmid, E.V., 1988, Exterior Durability of Organic Coatings, Fmj International Publications Limited, England.