Yıl 2018, Cilt: 52 Sayı : 3 Sayfalar 122 - 126 2018-09-01
Effects of coloring procedures on shear bond strength between resin cement and colored zirconia
İlkin TUNCEL,İşıl TURP
23 261

Öz DOI: 10.26650/eor.2018.440PurposeDebonding is expected as a frequent failuretype in zirconia restorations. Therefore the aim of the current study is toevaluate the shear bond strength between colored zirconia and resin cement. Materials and methodsThere were 11 groups evaluated eachcontaining 12 zirconia discs (15 mm x 12 mm x 1.6 mm). Groups were colored withthe colors A3, B1, C4, D2, and D4 of the VITA classical shade scale. Coloringprocedure was carried out for either 3 second or 60 seconds for the studygroups and the control group was left untreated. Specimens were then bonded totranslucent resin cement having a thickness of 3 mm and width of 3 mm. Theshear bond strength of the samples was measured in a universal testing machinewith a crosshead speed of 1 mm per minute. Two-way analysis of variance andTukey’s HSD test were used for pairwise comparisons. Also paired t-test wasused for comparing groups with the same color but having different shadingtimes.ResultsAny significant difference was not foundbetween the shear bond strengths of samples depending on whether color orshading times. Among the groups, B1 (60 seconds of coloring) had the highestbond strength (10.05 MPa), while A3 (60 seconds of coloring) showed the lowestbond strength (6.72 MPa). However, these differences were not statisticallysignificant.ConclusionColoring zirconia did not affect the shearbond strength between zirconia and resin cement.

Anahtar Kelimeler

Shear bond strength; ceramic; coloring; zirconia; resin cement
1. Tinschert J, Zwez D, Marx R, Anusavice KJ. Structural reliability of alumina-, feldspar-, leucite-, mica- and zirconia-based ceramics. J Dent 2000; 28: 529-35.2. Ardlin BI. Transformation-toughened zirconia for dental inlays, crowns and bridges: Chemical stability and effect of low-temperature aging on flexural strength and surface structure. Dent Mater 2002; 18: 590-5.3. Ichikawa Y, Akagawa Y, Nikai H, Tsuru H. Tissue compatibility and stability of a new zirconia ceramic in vivo. J Prosthet Dent 1992; 68: 322-6.4. Piconi C, Maccauro G. Zirconia as a ceramic biomaterial. Biomaterials 1999; 20: 1-25.5. Oilo M, Gjerdet NR, Tvinnereim HM. The firing procedure influences properties of a zirconia core ceramic. Dent Mater 2008; 24: 471-5.6. Blatz MB, Oppes S, Chiche G, Holst S, Sadan A. Influence of cementation technique on fracture strength and leakage of alumina all-ceramic crowns after cyclic loading. Quintessence Int 2008; 39: 23-32.7. Blatz MB, Sadan A, Kern M. Resin-ceramic bonding: A review of the literature. J Prosthet Dent 2003; 89: 268-74.8. Atsu SS, Kilicarslan MA, Kucukesmen HC, Aka PS. Effect of zirconium-oxide ceramic surface treatments on the bond strength to adhesive resin. J Prosthet Dent 2006; 95: 430-6.9. Derand T, Molin M, Kvam K. Bond strength of composite luting cement to zirconia ceramic surfaces. Dent Mater 2005; 21: 1158-62.10. Palacios RP, Johnson GH, Phillips KM, Raigrodski AJ. Retention of zirconium oxide ceramic crowns with three types of cement. J Prosthet Dent 2006; 96: 104-14.11. Chang J, Da Silva JD, Sakai M, Kristiansen J, Ishikawa-Nagai S. The optical effect of composite luting cement on all ceramic crowns. J Dent 2009; 37: 937-43.12. Hill EE. Dental cements for definitive luting: A review and practical clinical considerations. Dent Clin North Am 2007; 51: 643-58.13. Blatz MB, Sadan A, Maltezos C, Blatz U, Mercante D, Burgess JO. In vitro durability of the resin bond to feldspathic ceramics. Am J Dent 2004; 17: 169-72.14. Kern M, Wegner SM. Bonding to zirconia ceramic: Adhesion methods and their durability. Dent Mater 1998; 14: 64-71.15. Luthy H, Loeffel O, Hammerle CH. Effect of thermocycling on bond strength of luting cements to zirconia ceramic. Dent Mater 2006; 22: 195-200.16. Lohbauer U, Zipperle M, Rischka K, Petschelt A, Muller FA. Hydroxylation of dental zirconia surfaces: Characterization and bonding potential. J Biomed Mater Res B Appl Biomater 2008; 87: 461-7.17. Aboushelib MN, de Jager N, Kleverlaan CJ, Feilzer AJ. Microtensile bond strength of different components of core veneered all-ceramic restorations. Dent Mater 2005; 21: 984-91.18. Stevenson B, Ibbetson R. The effect of the substructure on the colour of samples/restorations veneered with ceramic: A literature review. J Dent 2010; 38: 361-8.19. Deville S, Gremillard L, Chevalier J, Fantozzi G. A critical comparison of methods for the determination of the aging sensitivity in biomedical grade yttria-stabilized zirconia. J Biomed Mater Res B Appl Biomater 2005; 72: 239-45.20. Hjerppe J, Narhi T, Froberg K, Vallittu PK, Lassila LV. Effect of shading the zirconia framework on biaxial strength and surface microhardness. Acta Odontol Scand 2008 ;66: 262-7.21. Pittayachawan P, McDonald A, Petrie A, Knowles JC. The biaxial flexural strength and fatigue property of lava y-tzp dental ceramic. Dent Mater 2007; 23: 1018-29.22. Aboushelib MN, Kleverlaan CJ, Feilzer AJ. Effect of zirconia type on its bond strength with different veneer ceramics. J Prosthodont 2008; 17: 401-8.23. Mosharraf R, Rismanchian M, Savabi O, Ashtiani AH. Influence of surface modification techniques on shear bond strength between different zirconia cores and veneering ceramics. J Adv Prosthodont 2011; 3: 221-8.24. Chevalier J, Deville S, Munch E, Jullian R, Lair F. Critical effect of cubic phase on aging in 3mol% yttria-stabilized zirconia ceramics for hip replacement prosthesis. Biomaterials 2004; 25: 5539-45.25. Chen PL, Chen IW. Grain boundary mobility in y2o3: Defect mechanism and dopant effects. J Am Ceram Soc 1996; 79: 1801-9.26. Blackman R, Barghi N, Duke E. Influence of ceramic thickness on the polymerization of light-cured resin cement. J Prosthet Dent 1990; 63: 295-300.27. Hasegawa EA, Boyer DB, Chan DC. Hardening of dual-cured cements under composite resin inlays. J Prosthet Dent 1991; 66: 187-92.28. Warren K. An investigation into the microhardness of a light cured composite when cured through varying thicknesses of porcelain. J Oral Rehabil 1990; 17: 327-34.29. Heffernan MJ, Aquilino SA, Diaz-Arnold AM, Haselton DR, Stanford CM, Vargas MA. Relative translucency of six all-ceramic systems. Part I: Core materials. J Prosthet Dent 2002; 88: 4-9.30. Moon JE, Kim SH, Lee JB, Ha SR, Choi YS. The effect of preparation order on the crystal structure of yttria-stabilized tetragonal zirconia polycrystal and the shear bond strength of dental resin cements. Dent Mater 2011; 27: 651-63.31. Kim MJ, Kim YK, Kim KH, Kwon TY. Shear bond strengths of various luting cements to zirconia ceramic: Surface chemical aspects. J Dent 2011; 39: 795-803.32. Komine F, Kobayashi K, Saito A, Fushiki R, Koizumi H, Matsumura H. Shear bond strength between an indirect composite veneering material and zirconia ceramics after thermocycling. J Oral Sci 2009; 51: 629-34.33. Kuriyama S, Terui Y, Higuchi D, Goto D, Hotta Y, Manabe A, Miyazaki T. Novel fabrication method for zirconia restorations: Bonding strength of machinable ceramic to zirconia with resin cements. Dent Mater J 2011; 30: 419-24.34. Lin J, Shinya A, Gomi H, Shinya A. Effect of self-adhesive resin cement and tribochemical treatment on bond strength to zirconia. Int J Oral Sci 2010; 2: 28-34.35. Takeuchi K, Fujishima A, Manabe A, Kuriyama S, Hotta Y, Tamaki Y, Miyazaki T. Combination treatment of tribochemical treatment and phosphoric acid ester monomer of zirconia ceramics enhances the bonding durability of resin-based luting cements. Dent Mater J 2010; 29: 316-23.36. Wegner SM, Kern M. Long-term resin bond strength to zirconia ceramic. J Adhes Dent 2000; 2: 139-47.
Birincil Dil en
Konular Sağlık Bilimleri ve Hizmetleri
Yayımlanma Tarihi 1 Eylül 2018
Bölüm Araştırmalar / Original Articles
Yazarlar
Tarihler

Yayımlanma Tarihi : 1 Eylül 2018


Makalenin Yazarları
İlkin TUNCEL
İşıl TURP